牌号简介 About |
---|
Fortus 3D生产系统的生产级热塑性塑料abs-m30比标准Stratasys abs高出25-70%,是概念建模、功能原型、制造工具和最终使用零件的理想材料。与标准ABS相比,ABS-M30具有更大的拉伸、冲击和弯曲强度。对于更耐用的零件,层间粘合比标准ABS强得多。这将导致更实际的功能测试和更高质量的最终使用部件。当与Fortus 3D生产系统结合使用时,ABS-M30为您提供了更强大、更平滑、功能更详细的真实零件。 Production-Grade Thermoplastic for Fortus 3D Production Systems ABS-M30 is up to 25-70 percent stronger than standard Stratasys ABS and is an ideal material for conceptual modeling, functional prototyping, manufacturing tools, and end-use-parts. ABS-M30 has greater tensile, impact, and flexural strength than standard ABS. Layer bonding is significantly stronger than that of standard ABS, for a more durable part. This results in more realistic functional tests and higher quality parts for end use. When combined with a Fortus® 3D Production System, ABS-M30 gives you Real Parts™ that are stronger, smoother, and with better feature detail. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ASTM D792 |
Thickness(Layer Capability) Thickness(Layer Capability) |
127.0 到 330.2 | µm | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
140 | J/m | ASTM D256-A |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
280 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
95.6 | ℃ | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ||
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 6 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
ASTM E831 | ||
MD MD |
1/℃ | ||
TD TD |
1/℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength 7 |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant 8 |
ASTM D150 | ||
耗散因数 Dissipation factor 9 |
ASTM D150 | ||
体积电阻 Volumetric resistance 10 |
ohms | ASTM D257 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
2.50 mm 2.50 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
拉伸模量 Tensile modulus 1 |
|||
3.18 mm 3.18 mm 1 |
MPa | ASTM D638 | |
拉伸强度 tensile strength 2 |
|||
3.18 mm 3.18 mm 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 3 |
|||
断裂,3.18 mm Fracture, 3.18 mm 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength 5 |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型 1, 0.20 in/min |
3 方法 I (三点负荷), 0.050 in/min |
4 标准 B (120°C/h), 载荷2 (50N) |
5 方法A(短时间) |
6 All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation. |
【新闻资讯】查看全部
亚马逊拒绝提出减少使用塑料的具体计划
2021-06-02 搜料网资讯: 亚马逊的股东们已经拒绝了关注环境问题的投资者迫使其详细说明其塑料包装的影响的企图。此次股东表决结果可能只是环保人士要求10家主要上市公司减少使用原生塑料 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |