牌号简介 About |
---|
ELITE™ 5401GT增强聚乙烯树脂是一种通过陶氏原位技术生产的共聚物。它具有极高的抗冲击性,结合优异的撕裂、拉伸和光学性能,适用于高强度吹塑薄膜应用。ELITE™ 5401GT增强聚乙烯树脂为自动包装应用提供了低密封起始温度、高模量和低堵塞倾向的独特组合。ELITE™ 5401GT增强聚乙烯树脂含有防滑和抗阻塞添加剂应用:食品和特种包装薄膜。非常坚硬的薄膜符合:欧盟,2011年第10号美国食品和药物管理局FCN 424,有关完整的详细信息,请参考法规。 ELITE™ 5401GT Enhanced Polyethylene Resin is a copolymer produced via INSITE™ Technology from Dow. It offers extremely high impact resistance, combined with excellent tear, tensile and optical properties for high strength blown film applications. ELITE 5401GT Enhanced Polyethylene Resin offers a unique combination of low seal initiation temperature and high modulus and low blocking tendency for automatic packaging applications. ELITE 5401GT Enhanced Polyethylene Resin contains slip and antiblock additives Applications: Food and specialty packaging films. Very tough thin gauge films Complies with: EU, No 10/2011 U.S. FDA FCN 424 Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.917 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
51 | µm | |
膜刺穿强度 Membrane puncture strength 2 |
|||
51 µm 51 µm 2 |
6.00 | J | ASTM D5748 |
膜刺穿力 Membrane puncture force 2 |
|||
51 µm 51 µm 2 |
80.0 | N | ASTM D5748 |
拉伸模量 Tensile modulus 2 |
|||
2% 正割,MD,51 µm 2% secant, MD, 51 µ m |
MPa | ||
2% 正割,TD,51 µm 2% secant, TD, 51 µ m |
MPa | ||
拉伸强度 tensile strength 2 |
|||
MD,屈服,51 µm MD, yield, 51 µ m |
MPa | ||
TD,屈服,51 µm TD, yield, 51 µ m |
MPa | ||
MD,断裂,51 µm MD, fracture, 51 µ m |
MPa | ||
TD,断裂,51 µm TD, fracture, 51 µ m |
MPa | ||
拉伸应变 Tensile strain 2 |
|||
MD,断裂,51 µm MD, fracture, 51 µ m |
% | ||
TD,断裂,51 µm TD, fracture, 51 µ m |
% | ||
落锤冲击 Drop hammer impact 2 |
|||
51 µm 51 µm 2 |
g | ISO 7765-1/B | |
埃尔曼多夫抗撕强度 Elmandorf tear strength 2 |
|||
MD:51 µm MD:51 µm |
g | ||
TD:51 µm TD:51 µm |
g | ||
始封温度 Initial sealing temperature 3 |
|||
51 µm 51 µm 3 |
℃ | 内部方法 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融温度 Melting temperature |
℃ | DSC | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss 2 |
|||
45°,51 µm 45°,51 µm 2 |
ASTM D2457 | ||
雾度 Haze 2 |
|||
51 µm 51 µm 2 |
% | ISO 14782 |
备注 |
---|
2、Blown film extruded at 232°C, 2.5:1 BUR, 1.8mm die gap. |
3、Blown film extruded at 232°C, 2.5:1 BUR, 1.8mm die gap. Temperature at which 5.25 N/15 mm heat seal strength is achieved. |
【新闻资讯】查看全部
石油巨头氢能替代步履维艰
2021-08-22 搜料网资讯: 长期以来,石油巨头一直宣称,氢能是减少碳排放的有效路径。新冠肺炎疫情全球暴发以后,石油巨头加速转型,并开始投入巨资追逐氢能项目。经过近1年的发展,石油巨 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |