| 牌号简介 About |
|---|
| Trirex是三养公司生产的聚碳酸酯树脂的注册商标。Trirex聚碳酸酯树脂具有优异的机械性能、良好的尺寸稳定性和高的电气性能，可广泛应用于电气、电子、电器、汽车和光学工业。TRIREX® 3026B(P)是一种聚碳酸酯树脂级，具有较高的低温冲击强度，结合优越的机械和物理性能。特点：优越的耐低温冲击性，良好的流动性，在广泛的温度范围内工作（-100°C~135°C），高电气性能，良好的尺寸稳定性，低吸水性，良好的耐候性，应用：TRIREX® 3026B(P)树脂级，用于挤出吹塑组件。高粘度。仅限透明色。 TRIREX is the registered trademark of polycarbonate resin manufactured by Samyang Corporation. TRIREX polycarbonate resins offer superior mechanical properties, good dimensional stability and high electrical performance, which allows it to be widely used for electrical, electronic, appliance, automotive and optical industries. TRIREX 3026B(P) is a polycarbonate resin grade which has high low temperature impact strength in combination with superior mechanical and physical property. Characteristics: Superior low temperature impact resistance Good flow-ability Workable under a wide range of temperatures (-100 °C ~ 135 °C) High electrical performance Good dimensional stability Low moisture absorbency Good weather resistance Applications: TRIREX 3026B(P) resin grade is used for extrusion blow molding components. High viscosity. Transparent colors only. |
产品描述 Product Description
用途：汽车领域的应用;电气/电子应用领域;光学应用;电器用具;
颜色：清晰/透明
加工条件：挤出吹塑成型
性能特点： 低吸湿性; 尺寸稳定性好; 高粘度; 耐低温冲击; 电气性好; 耐候抗UV; 易流动; Weather resistance is good,High Viscosity,Good liquidity,low-temperature impact resistance,Good Dimensional Stability,Low moisture absorption,Good Electrical Properties
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.20 | g/cm³ | ASTM D792 |
|
吸水率 Water absorption rate |
|||
|
24hr，23℃ 24hr，23℃ |
0.15 | % | ASTM D570 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
300℃，1.2kg 300℃，1.2kg |
2 | g/10min | ASTM D1238 |
|
模具收缩率 Mold shrinkage rate |
|||
|
3 mm 3 mm |
0.5 ~ 0.7 | % | ASTM D-955 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
68.6 | MPa | ASTM D638 |
|
断裂伸长率 elongation at break |
% | ASTM D638 | |
|
弯曲强度 bending strength |
|||
|
屈服 yield |
MPa | ASTM D790 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD MD |
cm/cm/℃ | ASTM D696 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻 Volumetric resistance |
Ω.cm | ASTM D257 | |
|
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
|
耐电弧性 Arc resistance |
sec | ASTM D495 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
|||
|
1.59 mm 1.59 mm |
UL 94 | ||
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
J/m | ASTM D256 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部 
朗盛:任命Jens-Christian Blad为企业展开总监
2017-05-09 特殊化学品公司朗盛刚为其企业发展部门任命了新一任主管。Jens-Christian Blad(39岁)最迟将于2017年9月1日开始负责该部门的运作。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付