| 牌号简介 About |
|---|
| 符合ISO 1043-1的材料规范：用20%长的玻璃纤维增强聚丙烯共聚物。低排放。纤维与聚丙烯基体发生化学耦合。球团是圆柱形的，通常和嵌入的纤维一样长10毫米。Celstran成型件具有高强度、高刚度、高热变形等优异的力学性能。由于部件中内置了纤维骨架，因此在高温和低温下缺口冲击强度会增加。长纤维增强能显著降低蠕变。模制品的各向同性收缩使翘曲最小化。通过注射成型，可以制造出具有高再现性的复杂零件。应用领域：汽车功能/结构件 Material code according to ISO 1043-1: PP Polypropylene copolymer reinforced with 20 weight percent long glass fibers. Low emission. The fibers are chemically coupled to the polypropylene matrix. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Application field: Functional/structural parts for automotive |
产品描述 Product Description
用途：汽车领域的应用;
加工条件：注射成型 Injection Molding
性能特点： 机械强度好; 化学耦合; 共聚物; 低VOC; 耐低温冲击; 各向同性好; 低翘曲性; 韧性好; Good Rigidity,Low warping,Good flexibility,Low odor,Chemical coupling,Copolymer,low-temperature impact resistance,Good Isotropy
填料：玻璃纤维 20
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.03 | g/cm³ | ISO 1183 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
4700 | MPa | ISO 527-2/1A |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
84.0 | MPa | ISO 527-2/1A/5 |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
2.5 | % | ISO 527-2/1A/5 |
|
弯曲模量 Bending modulus |
|||
|
23℃ 23℃ |
4500 | MPa | |
|
80℃ 80℃ |
MPa | ||
|
弯曲强度 bending strength |
|||
|
23℃ 23℃ |
MPa | ||
|
80℃ 80℃ |
MPa | ||
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
-30℃ -30℃ |
kJ/m² | ||
|
23℃ 23℃ |
kJ/m² | ||
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
-30℃ -30℃ |
kJ/m² | ||
|
23℃ 23℃ |
kJ/m² | ||
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
| 备注 | |||
|---|---|---|---|
| 暂无数据 | |||
|
【新闻资讯】查看全部
德研制出可用于皮下准确施药的新型资料
2016-02-23 德国弗赖堡大学19日宣布，该校研究人员研制出一种可用于皮下精确施放药物的新型复合材料，人体对这种材料不会产生不良反应。未来新材料有望用于治疗肿瘤等疾病。 研究人员用原子层沉积的方法将氧化锌植入聚乙二醇薄膜中，形成了一种可水解的复合材料。这种材料薄膜厚度只有几微米，其分子结构适合储存相对大剂量的药物。为了让这种储药材料可以精确施放药物，其表面还被镀上了两层导电聚合物。 研究人员将这种复合材料形象地描绘为一张多孔的网，上面的孔在施加负电时会打开，加正电时则关闭， |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |