| 牌号简介 About |
|---|
| 15 mfi阻燃剂，具有紫外线和释放功能，无氯无溴阻燃系统，符合RoHS标准的应用/用途：注塑外壳和通信设备、电子和电气设备、电器的组件。关键词：聚合物；热塑性塑料；聚碳酸酯（PC）；未增强、无氯无溴阻燃、冲击改性聚碳酸酯 15 MFI Flame Retardant, with UV and Release, Non-chlorine non-bromine FR system, RoHS compliant Application/Use: Injection molded housings and components of communications equipment, electronics and electrical devices, appliances. Key Words: Polymer; Thermoplastic; Polycarbonate (PC); Polycarbonate, Unreinforced, Non chlorine Non Bromine Flame Retardant, Impact Modified |
产品描述 Product Description
用途：电气/电子应用领域;外壳;电器用具;
加工条件：注射成型 Injection Molding
性能特点： 无卤; 含脱模剂; 阻燃; 耐候抗UV; Weather resistance is good,Halogen free,Good stripping performance,Flame Characteristics
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.23 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
300℃，1.20kg 300℃，1.20kg |
15 | g/10min | ASTM D1238 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.50 到 0.70 | % | ASTM D955 |
|
室外适用性 Outdoor applicability |
f1 | UL 746C | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
3.2mm 3.2mm |
750 | J/m | ASTM D256 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ||
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：-40~95℃ MD：-40~95℃ |
1/℃ | ||
|
TD：-40~95℃ TD：-40~95℃ |
1/℃ | ||
|
相对温度指数 Relative temperature index |
℃ | UL 746 | |
|
电气性能 Electrical performance |
℃ | UL 746 | |
|
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
|||
|
23℃ 23℃ 3 |
ohms·cm | ||
|
90 ℃ 90 ℃ 4 |
ohms·cm | ||
|
介电强度 Dielectric strength |
|||
|
3.18 mm 3.18 mm |
kV/mm | ASTM D149 | |
|
耐电弧性 Arc resistance |
ASTM D495 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
|
高电弧燃烧指数（HAI） High Arc Burning Index (HAI) |
|||
|
1.5 mm 1.5 mm |
|||
|
3.0 mm 3.0 mm |
|||
|
高电压电弧起痕速率 High voltage arc marking rate |
|||
|
HVTR HVTR |
UL 746 | ||
|
热丝引燃 Hot wire ignition |
|||
|
HWI HWI |
|||
|
1.5 mm 1.5 mm |
|||
|
3.0 mm 3.0 mm |
|||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
|||
|
1.50 mm 1.50 mm |
|||
|
2.50 mm，黑色，灰色，褐色 2.50 mm, black, gray, brown |
|||
|
3.00 mm，所有颜色 3.00 mm, all colors |
|||
|
灼热丝可燃性指数 Glowing wire flammability index |
℃ | IEC 60695-2-12 | |
|
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 | |
|
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
UL Rating UL Rating |
|||
|
Non-bromine，Non-chlorine Non-bromine，Non-chlorine |
UL 746H | ||
|
RoHS Compliance RoHS Compliance |
UL 746R | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
|
拉伸强度 tensile strength |
|||
|
屈服，3.17 mm Yield, 3.17 mm |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂，3.17 mm Fracture, 3.17 mm |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
|||
|
3.17 mm 3.17 mm |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
|||
|
屈服，3.17 mm Yield, 3.17 mm |
MPa | ASTM D790 | |
| 备注 |
|---|
| 3、40 hr @ 50% RH |
| 4、96 hr @ 50% RH |
|
【新闻资讯】查看全部 
赣锋锂业拟收购Millennial股权
2021-07-31 搜料网资讯： 近日，江西赣锋锂业股份有限公司发布公告，公司董事会于7月16日审议通过了《关于赣锋国际或其全资子公司对加拿大Millennial公司进行要约收购涉及矿业权投资的议案》， |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付