WELLAMID Nylon 6600 MR 209 HWCP是一种聚酰胺66(尼龙66)材料,含有的填充物为矿物填料。 该产品在欧洲有供货,。 WELLAMID Nylon 6600 MR 209 HWCP的主要特性有: 阻燃/额定火焰 热稳定剂 WELLAMID Nylon 6600 MR 209 HWCP is a Polyamide 66 (Nylon 66) material filled with mineral. It is available in Europe. Important attributes of WELLAMID Nylon 6600 MR 209 HWCP are: Flame Rated Heat Stabilizer |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸应变 Tensile Strain Tensile Strain |
|||
断裂 brk,干燥 dry Broken BRK, dry dry |
8 | MPa | ISO 527 |
断裂 brk,湿润 cond. Broken BRK, wet Cond |
18 | MPa | ISO 527 |
拉伸强度 Tensile Strength Tensile Strength |
|||
干燥 dry Dry |
85 | % | ISO 527-2 |
湿润 cond. Wet Cond |
55 | % | ISO 527-2 |
拉伸模量 Tensile Modulus Tensile Modulus |
|||
干燥 dry Dry |
4300 | MPa | ISO 527 |
湿润 cond. Wet Cond |
MPa | ISO 527 | |
弯曲模量 Flexural Modulus Flexural Modulus |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy notched Impact strength Charpy Notched Impact Strength |
|||
23℃,干燥 dry 23 ℃, dry |
kJ/m² | ISO 179 | |
23℃,湿润 cond. 23 ℃, moist cond |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotched Impact strength Charpy Unnotch Impact strength |
|||
23℃,干燥 dry 23 ℃, dry |
kJ/m² | ISO 179 | |
23℃,湿润 cond. 23 ℃, moist cond |
kJ/m² | ISO 179 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature Melting temperature |
℃ | ||
热变形温度 HDT Hot deformation temperature HDT |
|||
A A |
℃ | ISO 75-1/-2 | |
B B |
℃ | ISO 75-1/-2 | |
维卡软化温度 Vicat Softening Temperature Vicat Softening Temperature |
℃ | ISO 306/B | |
线性热膨胀系数 Coeff.of linear therm expansion Coeff. of linear thermal expansion |
|||
23℃-80℃ 23℃-80℃ |
×10-4/K | DIN 53752 | |
电气性能 ELECTRICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相对电容率 Relative Permittivity Relative permittivity |
|||
干燥 dry Dry |
1 MHz | IEC 60250 | |
湿润 cond. Wet Cond |
1 MHz | IEC 60250 | |
耗散因数 Dissipation Factor Dissipation Factor |
|||
干燥 dry Dry |
1 MHz | IEC 60250 | |
湿润 cond. Wet Cond |
1 MHz | IEC 60250 | |
耐电强度 Electric strength Electric strength |
|||
干燥 dry Dry |
kV/mm | IEC 60243-1 | |
湿润 cond. Wet Cond |
kV/mm | IEC 60243-1 | |
相比漏电起痕指数 Comparative Tracking Index Compared Tracking Index |
|||
干燥 dry Dry |
V | IEC 60112 | |
体积电阻率 Volume Resistivity Volume Resistance |
|||
干燥 dry Dry |
ohm·cm | IEC 60093 | |
湿润 cond. Wet Cond |
ohm·cm | IEC 60093 | |
表面电阻率 Surface Resistivity Surface Resistivity |
|||
干燥 dry Dry |
ohm | IEC 60093 | |
湿润 cond. Wet Cond |
ohm | IEC 60093 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density Density |
g/cm³ | ISO 1183 | |
模具收缩率 Mold Shrinkage Mold Shrinkage |
% | ||
饱和值 saturation value at Saturation value at |
% | DIN 53495 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame Class Rating Flame Class Rating |
|||
1.6 mm 1.6 mm |
UL 94 | ||
1.6 mm 1.6 mm |
UL 94 | ||
3.2 mm 3.2 mm |
UL 94 | ||
3.2 mm 3.2 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
美的收购德国库卡 首战告捷
2016-07-28 美的集团(000333.SZ,下称美的)7月20日下午宣布了要约收购德国机器人巨头库卡首阶段的成果――截止到7月15日,接受美的要约的库卡股份达72.18%,加上美的原来持有的库卡13.51%的股份,这意味着美的将可控股库卡85.69%,首战告捷。 美的董事长兼总裁方洪波表示:“今天是美的与库卡深化合作关系的重要里程碑,我们的合作将进一步提升双方公司的价值。美的此前与库卡所签订的投资协议主导着我们的合作关系。我们将继续支持库卡的业务并增进其市场发展,尤其是在中国市场的发展。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |