| 牌号简介 About |
|---|
| HOMO-PLA：基于PURAC单体的通用聚乳酸混合物：耐热性高达120°C（HDT B），良好的加工经济性，抗冲击性，可与ABS生物基含量相媲美，多种使用寿命终止的选择，现有的商业可用性混合物A：这一改进的关键驱动力是聚乳酸均聚物，它们已经通过h少量PDLA均聚物和传统核素（详情见下表中的混合物A）。在不添加大量填料的情况下，混合物A的热性能得到提高。 Homo PLA: general purpose PLA blends based on monomers from Purac offer: Heat resistance up to 120°C (HDT B) Good processing economics Impact resistance comparable to ABS Biobased content Multiple end-of-life options Existing commercial availability Blend A: the key driver behind this improvement are PLLA homopolymers that have been nucleated with a small amount of PDLA homopolymers and a traditional nucleant (see blend A in the table below for more details). The increased heat performance of blend A was obtained without adding significant amounts of filler. |
产品描述 Product Description
用途：通用;
加工条件：注射成型 Injection Molding
性能特点： 成核的; 可回收; 耐高温; 均聚物; Renewable resources,Nucleation,High Heat Resistance,Homopolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.24 | g/cm³ | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
3000 | MPa | |
|
拉伸强度 tensile strength |
45.0 | MPa | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
5.0 | % | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
23℃ 23℃ |
5.0 | kJ/m² | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature 2 |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed 2 |
℃ | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 平放 |
|
【新闻资讯】查看全部 
中化蓝天投资1.7亿建三氟氯乙烯项目
2016-12-23 中化蓝天投资1.7亿元，正式在湖南郴州开工建设三氟氯乙烯项目一期工程。 这是中化蓝天在郴州打造氟化工完整产业链的一个重要项目。据报道，该公司表示，未来5年将依托郴州丰富的萤石资源，再投入20亿元，实现氟化 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付