牌号简介 About |
---|
LLT12是一种1-丁烯为基础的LLDPE级产品,采用滚球技术生产。LL T12可用于低压电力电缆绝缘,采用硅烷交联工艺。这是赤脚等级,必须适当添加以满足最终使用要求。聚合过程中实现的精确形态控制提供了优越的加工性能和改进的性能。 LL T12 is a 1-butene based LLDPE grade produced by the Spherilene Technology. LL T12 can be used for Low Voltage power cable insulation, using silane-crosslinking process. This is a barefoot grade and has to be suitably additivated for end use requirements. The precise morphological control achieved during polymerization confers superior processability and improved performance properties. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
0.926 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
3.7 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 3 |
|||
断裂,模压成型 Fracture, molded 3 |
20.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain 3 |
|||
断裂,模压成型 Fracture, molded 3 |
1000 | % | ASTM D638 |
弯曲模量 Bending modulus |
550 | MPa | ASTM D790 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,模压成型 23 ℃, molded |
J/m | ASTM D256-A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 23°C |
3 类型 4 |
【新闻资讯】查看全部
科思创在泰国启动新的聚碳酸酯薄膜生产线
2020-10-12 搜料网资讯: 科思创在泰国Map Ta Phut工业区启动了一条新的聚碳酸酯(PC)薄膜生产线。凭借新的产能,该公司旨在满足亚太地区快速增长的需求,并巩固自身在该领域的市场领导者地位 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |