| 牌号简介 About |
|---|
| NORYL™ GFN3F resin是 PPE+PS混合物。30%玻璃纤维增强。符合NSF 61，FDA合规性。吸水率低、水解稳定性。尺寸稳定性。适用于流体工程应用，包括泵壳、泵叶轮和水表部件 PPE+PS blend. 30% Glass reinforced. NSF 61 listing in several colors (restrictions apply). FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including pump housings, pump impellers and water meter components. |
产品描述 Product Description
用途：织物;通用;单丝;皮带材料;
加工条件：细丝挤出
性能特点： 防火阻燃等级HB; 熔体稳定性高; 均聚物; 食品接触; 水携带性低; 光学性能; Optical performance,Food contact compliance,Low water portability,Homopolymer,Higher melt stability,HB
填料：玻璃纤维 30
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.29 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
300℃，5.0kg 300℃，5.0kg |
8.7 | g/10min | ASTM D1238 |
|
熔体体积流动速率 Melt Volume Rate |
|||
|
300℃，5 kg 300℃，5 kg |
7.82 | cm³/10min | ISO 1133 |
|
收缩率 Shrinkage rate |
|||
|
MD：3.2 mm MD：3.2 mm |
0.10 to 0.40 | % | 内部方法 |
|
吸水率 Water absorption rate |
|||
|
24hr 24hr |
0.060 | % | ASTM D570 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/2C | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/2C | |
|
23℃ 23℃ |
kJ/m² | ISO 179/2C | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
|
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
|
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
|
23℃ 23℃ |
J/m | ASTM D4812 | |
|
-30℃ -30℃ |
J/m | ASTM D256 | |
|
23℃ 23℃ |
J/m | ASTM D256 | |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
|
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ISO 180/1U | ||
|
-30℃ -30℃ |
kJ/m² | ISO 180/1U | |
|
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
ASTM D648 | ||
|
1.8 MPa，未退火，64 mm跨距 1.8 MPa, unannealed, 64 mm span |
℃ | ISO 75-2/Af | |
|
0.45 MPa，未退火，64 mm跨距 0.45 MPa, unannealed, 64 mm span |
℃ | ISO 75-2/Bf | |
|
1.8 MPa，未退火，3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
1.8 MPa，未退火，6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
|
0.45 MPa，未退火，3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
|
0.45 MPa，未退火，6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
B50 B50 |
℃ | ISO 306 | |
|
B120 B120 |
℃ | ISO 306/B120 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
TD：-40~40℃ TD：-40~40℃ |
1/℃ | ASTM E831 | |
|
MD：-40~40℃ MD：-40~40℃ |
1/℃ | ASTM E831 | |
|
相对温度指数 Relative temperature index |
|||
|
电气性能 Electrical performance |
℃ | UL 746 | |
|
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
|
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
介电强度 Dielectric strength |
|||
|
3.2 mm，在油中 3.2 mm in oil |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
ASTM D150 | ||
|
50 Hz 50 Hz |
ASTM D150 | ||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
ASTM D150 | ||
|
50 Hz 50 Hz |
ASTM D150 | ||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
耐电弧性 Arc resistance |
ASTM D495 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
|
高电弧燃烧指数（HAI） High Arc Burning Index (HAI) |
UL 746 | ||
|
高电压电弧起痕速率 High voltage arc marking rate |
|||
|
HVTR HVTR |
UL 746 | ||
|
热丝引燃 Hot wire ignition |
|||
|
HWI HWI |
UL 746 | ||
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
|||
|
1.50 mm 1.50 mm |
UL 94 | ||
|
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
MPa | ASTM D638 | |
|
断裂 fracture |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
断裂 fracture |
% | ISO 527-2 | |
|
弯曲模量 Bending modulus |
ASTM D790 | ||
|
50 mm跨距 50 mm span |
MPa | ASTM D790 | |
|
100 mm跨距 100 mm span |
MPa | ASTM D790 | |
|
弯曲模量 Bending modulus |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
ASTM D790 | ||
|
屈服，50 mm跨度 Yield, 50 mm span |
MPa | ASTM D790 | |
|
屈服，100 mm跨度 Yield, 100 mm span |
MPa | ASTM D790 | |
|
洛氏硬度 Rockwell hardness |
|||
|
L 级 Level L |
ASTM D785 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
|
【新闻资讯】查看全部
亨斯迈助意大利Forestali造皮革行业用复合资料
2016-03-04 意大利Industrie Chimiche Forestali S.p.A 公司利用亨斯迈的特等热塑性聚氨酯(简称TPU)研发了一种用于皮革制品的新型复合材料。 该复合材料被称为“Tintoretto”，采用双层TPU材质，能够增强高端皮革制品，例如设计师手袋和腰带的结构的完整性。 Forestali是皮革制品、制鞋、帆船和家具行业专用胶黏剂生产商，还生产多种类的浸染织物及纺织品。当觅得皮革产品市场的一处新商机时，Forestali随即联系了它的一个长期供应 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |