| 牌号简介 About |
|---|
| Adflex Z 108 S是一种反应器TPO（热塑性聚烯烃），采用Lyondellbasell专有的Catalloy工艺技术制造。Adflex Z 108 S具有非常高的柔软度、非常低的弯曲模量和较高的熔体流动速率。它用于注塑、冲击改性、挤出涂层、软复合、薄膜和纤维应用。它也适用于在不改变透明度的情况下对聚丙烯均聚物和无规共聚物进行改性。该等级为天然颗粒形式。有关法规遵从性信息，请参阅Adflex Z 108 S产品管理公告（PSB）。 Adflex Z 108 S is a reactor TPO (thermoplastic polyolefin) manufactured using the proprietary Catalloy process technology from LyondellBasell. Adflex Z 108 S features a very high softness, a very low flexural modulus and a high melt flow rate. It is used by customers for injection molding, impact modification, extrusion coating, soft compounding, film and fiber applications. It is also selected by customers for the modification of polypropylene homopolymer and random copolymer without altering the transparency. The grade is available in natural pellet form. |
产品描述 Product Description
用途：薄膜;塑料改性;流延薄膜;卫浴产品;复合;纤维;
颜色：自然色
加工条件：复合
性能特点： 拉伸性能好; 柔软性好; 耐低温冲击; 流动性高; High liquidity,Good Tensile Strength,Soft,low-temperature impact resistance
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.890 | g/cm³ | ISO 1183/A |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
27 | g/10min | ISO 1133 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
ISO 868 | ||
|
邵氏 A，15 秒 Shore A, 15 seconds |
85 | ISO 868 | |
|
邵氏 D，15 秒 Shore D, 15 seconds |
30 | ISO 868 | |
|
拉伸强度 tensile strength |
|||
|
断裂 fracture |
6.00 | MPa | ISO 527-2 |
|
屈服 yield |
MPa | ISO 527-2 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ISO 527-2 | |
|
屈服 yield |
% | ISO 527-2 | |
|
弯曲模量 Bending modulus |
MPa | ISO 178 | |
|
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
撕裂强度 tear strength 2 |
kN/m | ASTM D624 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
|
-40℃ -40℃ |
kJ/m² | ISO 180-1A | |
|
23℃ 23℃ |
ISO 180/1A | ||
|
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 3 |
ASTM D3763 | ||
|
-40℃，3.20 mm，Energy at Peak Load，Ductile Failure -40℃，3.20 mm，Energy at Peak Load，Ductile Failure |
J | ASTM D3763 | |
|
23℃，3.20 mm，Energy at Peak Load，Ductile Failure 23℃，3.20 mm，Energy at Peak Load，Ductile Failure |
J | ASTM D3763 | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
|
韧性/脆性转变温度 Toughness/brittle transition temperature |
℃ | ISO 6603-2 | |
|
维卡软化温度 Vicat Softening Temp |
|||
|
A50 A50 |
℃ | ISO 306/A50 | |
|
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
60°，3200 µm，注塑成型 60 °, 3200 µ m, injection molding |
ASTM D2457 | ||
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 C 模具, 2.0 in/min |
| 3 7.22 ft/sec |
|
【新闻资讯】查看全部
第三十二届中国国际塑料橡胶工业展览会
2018-05-15 近日，由上海石油化工研究院(以下简称上海院)自主研发的PBST改性薄膜专用料、热塑性淀粉母料和生物基降解薄膜专用料三类专用料及其薄膜制品亮相第三十二届中国国际塑料橡胶工业展览会(CHINAPLAS2018)，与合作单位仪征化纤共同参展。参展材料吸引众多参观人员前来咨询。 科技创新是推动人类社会发展的不竭动力，而材料是实现技术应用价值过程中不可或缺的关键要素。本届展览会围绕“创新塑造未来”主题，聚焦“智能制造、高新材料、环保科技”，携手全球40多个国家及地区的4000多家参展 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |