QC-8144是一种低密度(0.043 lb/in³)乙烯基酯基片状模塑料(SMC),设计用于要求高结构强度、耐腐蚀性和耐温性以及低模密度的部件的压塑。 QC-8144 is a low-density (0.043 lb/in³) vinyl ester based sheet molding compound (SMC) designed for compression molding of components requiring high structural strength, corrosion resistance and temperature resistance combined with low molded density. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
0.10 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.13 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
117 | MPa | ASTM D638 |
弯曲模量 Bending modulus |
6890 | MPa | ASTM D790 |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
贮藏期限 Storage period |
|||
24℃ 24℃ |
wk | ||
脱模时间 stripping time |
|||
149℃ 149℃ |
min |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
海天国际财报:毛利率及运营利润均小幅上升
2016-03-11 海天国际控股有限公司于3月9日发布2015年财报,数据显示, 2015年海天国际收入为73.364亿人民币,较2014年减少3%,但是毛利率从2014年的32.4%增加至33%;2015年经营利润为15.455亿人民币,同比增幅为4.0%。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |