| 牌号简介 About |
|---|
| Jampilen HP422H是为高速生产BOPP薄膜而设计的一种改性均聚物，其具有优异的挤出稳定性、厚度变化控制、很高的可拉伸性和双向取向准备。该产品具有增强的加工稳定性和低水携带性能。Jampilen HP422H不含任何滑脱剂或抗静电剂，不含硬脂酸钙。该产品特别适用于金属化薄膜。用Jampilen HP422H生产的BOPP薄膜具有良好的机械性能，即使在低温下，也具有良好的防潮、防臭、防油、防氧、透明度和光泽。由Jampilen HP422H制成的单层或共挤薄膜，厚度在20到40微米之间，用于食品、化妆品和录像带的包装。 "Jampilen HP422H" is a modified homopolymer designed for the high speed production of BOPP films, wherein an outstanding extrusion stability, thickness variation control, a very high drawability and readiness to a two way orientation would be achieved. The product contains a reinforced processing stabilization and features low water carry-over properties. "Jampilen HP422H" does not contain any slip or antistatic agent and is Calcium Stearate free. The Product is particularly suitable for metalizing film.BOPP films produced with "Jampilen HP422H" feature goodmechanical properties, even at low temperatures, excellentbarrier against moisture, odors, oils and oxygen and goodtransparency and gloss.Monolayer or coextruded films made of "Jampilen HP422H" with a thickness ranging from 20 to 40 µm are used for the packaging of foodstuffs, cosmetics, CDs and DVDs. Features: High impact strength High puncture resistance Good transparency and gloss Homopolymer Typical Applications: Food packaging film Packaging of cosmetics, CDs and DVDs Barrier film |
产品描述 Product Description
用途：母料;玩具;食品包装;双向拉伸薄膜;媒介包装;化妆品包装;薄壁包装;厨具;
加工条件：薄膜挤出 Film extrusion
性能特点： 防潮; 成型周期快; 保持香味; 易剥离; 易加工; 低透气性; 耐油; 阻隔树脂; 均聚物; 电镀; 透光性好; 冲击性能好; 表面光泽度好; 水携带性低; 抗穿孔性; Excellent Processability,Good Clarity,Good surface appearance,High impact resistance,Good dissection,Retention of aroma ,Quick molding cycle,Low odor,Moisture resistance,Electroplating,Grease resistance,Block resin,Puncture Resistant,Low water portability,Homopolymer
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.900 | g/cm³ | ASTM D1505 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
230℃，2.16kg 230℃，2.16kg |
2.1 | g/10min | ASTM D1238 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃ 23℃ |
60 | J/m | ASTM D256 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，未退火 0.45 MPa, unannealed |
92.0 | ℃ | ASTM D648 |
|
维卡软化温度 Vicat Softening Temp |
154 | ℃ | ASTM D1525 2 |
|
加速干燥箱老化 Accelerate oven aging |
|||
|
150℃ 150℃ |
hr | ASTM D3012 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
雾度 Haze |
|||
|
20 µm 20 µm |
% | ASTM D1003 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
R 级 R-level |
ASTM D785 | ||
|
拉伸强度 tensile strength |
|||
|
屈服 yield |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 压 力1 (10N) |
|
【新闻资讯】查看全部 
法雷奥拟收购德国汽车电子供应商佩科
2015-12-25 法国零部件供应商法雷奥(Valeo) 日前宣布，该公司将收购德国车内电子与移动连接供应商佩科(Peiker)。本次收购中法雷奥将整合佩科在德国的700名员工，其中包括150名高级工程师。届时法雷奥将扩大其在德国的业务，同 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付