牌号简介 About |
---|
Eastman Tritan™ FX100是一种无定形共聚酯,具有优异的透明度和韧性,以及优异的耐热性和耐化学性。由这一新一代共聚酯制成的薄膜可以在不预先干燥的情况下进行热成型,并且具有宽的处理窗口,允许反映复杂细节的产品设计。Eastman Tritan™ FX100共聚酯可用于美国食品药品监督管理局(FDA)规定的重复使用食品接触物品中。Eastman Tritan™ FX100共聚酯通过了食品设备材料NSF/ANSI标准51的认证。 Eastman Tritan™ FX100 is an amorphous copolyester that combines excellent clarity and toughness with outstanding heat and chemical resistance. Films manufactured from this new-generation copolyester can be thermoformed without pre-drying and with a wide processing window that allows for product designs that reflect intricate detail. Eastman Tritan™ FX100 copolyester may be used in repeated use food contact articles under United States Food and Drug Administration (FDA) regulations. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.19 | g/cm³ | ASTM D792 |
吸水率 Water absorption rate |
|||
23℃,24hr,0.25 mm 23℃,24hr,0.25 mm |
0.50 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
耐磨耗性 Wear resistance 2 |
|||
23℃ 23℃ 2 |
23haze | % | ASTM D1044 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
250 | µm | |
膜刺穿强度 Membrane puncture strength 3 |
|||
250 µm 250 µm 3 |
4.60 | J | ASTM D3763 |
割线模量 Secant modulus |
ASTM D882 | ||
MD:250 µm MD:250 µm |
MPa | ASTM D882 | |
TD:250 µm TD:250 µm |
MPa | ASTM D882 | |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,屈服,250 µm MD, yield, 250 µ m |
MPa | ASTM D882 | |
TD,屈服,250 µm TD, yield, 250 µ m |
MPa | ASTM D882 | |
MD,断裂,250 µm MD, fracture, 250 µ m |
MPa | ASTM D882 | |
TD,断裂,250 µm TD, fracture, 250 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,屈服,250 µm MD, yield, 250 µ m |
% | ASTM D882 | |
TD,屈服,250 µm TD, yield, 250 µ m |
% | ASTM D882 | |
MD,断裂,250 µm MD, fracture, 250 µ m |
% | ASTM D882 | |
TD,断裂 TD, fracture |
% | ASTM D882 | |
落锤冲击 Drop hammer impact 4 |
ASTM D1709A | ||
-30℃,250 µm -30℃,250 µm |
g | ASTM D1709-A | |
23℃,250 µm 23℃,250 µm |
g | ASTM D1709-A | |
裤型撕裂耐性 Pant tear resistance 5 |
ISO 6383-1 | ||
MD:250 µm MD:250 µm |
N/mm | ISO 6383-1 | |
TD:250 µm TD:250 µm |
N/mm | ISO 6383-1 | |
透氧率 Oxygen permeability |
|||
23℃,250 µm,50% RH 23℃,250 µm,50% RH |
cm³·mm/m²/atm/24 hr | ASTM D3985 | |
水气透过率 Water vapor transmittance |
ASTM F1249 | ||
23℃,100% RH,250 µm 23℃,100% RH,250 µm |
g/m²/24 hr | ASTM F1249 | |
38℃,100% RH,250 µm 38℃,100% RH,250 µm |
g/m²/24 hr | ASTM F1249 | |
二氧化碳渗透性 Carbon dioxide permeability 6 |
|||
23℃,254.0 µm 23℃,254.0 µm 6 |
cm³·mm/m²/atm/24 hr | ASTM D1434 | |
撕裂强度 tear strength |
|||
MD,23℃,250 µm MD,23℃,250 µm |
N | ASTM D1922 | |
TD,23℃,250 µm TD,23℃,250 µm |
N | ||
PPT撕裂阻力 PPT tear resistance |
ASTM D2582 | ||
MD:23℃,250.0 µm MD:23℃,250.0 µm |
N | ASTM D2582 | |
TD:23℃,250.0 µm TD:23℃,250.0 µm |
N | ASTM D2582 | |
抗撕裂蔓延性 Tear resistant vine ductility 7 |
ASTM D1938 | ||
MD:23℃,250.0 µm MD:23℃,250.0 µm |
gf | ASTM D1938 | |
TD:23℃,250.0 µm TD:23℃,250.0 µm |
gf | ASTM D1938 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
撕裂强度 tear strength |
ASTM D1938 | ||
开裂 cracking 8 |
kN/m | ASTM D1938 | |
开裂 cracking 9 |
kN/m | ASTM D1938 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融温度 Melting temperature |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23℃,0.25 mm MD:23℃,0.25 mm |
1/℃ | ASTM D696 | |
比热 specific heat |
DSC | ||
60℃ 60℃ |
J/kg/℃ | DSC | |
100℃ 100℃ |
J/kg/℃ | DSC | |
150℃ 150℃ |
J/kg/℃ | DSC | |
200℃ 200℃ |
J/kg/℃ | DSC | |
250℃ 250℃ |
J/kg/℃ | DSC | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
60°,250 µm 60°,250 µm |
ASTM D2457 | ||
折射率 Refractive index |
ASTM D542 | ||
透光率 Transmittance |
|||
250 µm 250 µm |
% | ASTM D1003 | |
雾度 Haze |
|||
250 µm 250 µm |
% | ASTM D1003 | |
黄度指数 Yellowness index |
|||
250 mm 250 mm |
YI | ASTM D1925 | |
UV透过率(250.0 µm) UV transmittance (250.0 µ m) 10 |
% | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面能 Surface energy |
ASTM D5946 | ||
Dispersive:23℃,250.0 µm Dispersive:23℃,250.0 µm |
dyne/cm | ASTM D5946 | |
Polar:23℃,250 mm Polar:23℃,250 mm |
dyne/cm | ASTM D5946 | |
Total:23℃,250.0 µm Total:23℃,250.0 µm |
dyne/cm | ASTM D5946 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 average at 25 cycles |
3 Dynatup, Total Energy |
4 12.7 mm dia. head, 127 mm dia. clamp, 600 mm drop |
5 7.9 in/min |
6 50% RH |
7 254 mm/min |
8 TD, 250 µm |
9 MD, 250 µm |
10 % Transmission at 380 nm |
【新闻资讯】查看全部
废塑预想过环保关,必先处理设备与利润的投入产出比
2018-03-01 塑料诞生近100年来,给人类社会生活、生产带来方便的同时,也导致大量的废旧塑料垃圾,其难降解性对环境的影响也愈加明显,亟需正确处理。尤其是近年来国家一直积极推行环保治理,对于企业排污以及垃圾的处理上紧抓严防,废塑料行业更是环保的重点关注对象。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |