| 牌号简介 About |
|---|
| f010-h2o-00饮用水涂层系统NSF/ANSI 61认证Vipel® F010-H2O-00通过NSF/ANSI 61认证，用于商用和家用饮用水系统，作为保护屏障材料。如果制造商遵循第3页列出的成分和工艺说明，他们不需要进行额外的测试来制造符合NSF/ANSI 61标准的涂层。适用于次氯酸钠安全壳的优点Vipel® F010-H2O-00的配方也适用于次氯酸钠（氯漂白剂）安全壳。次氯酸钠是一种广泛接受的净水化学物质，对大多数金属和许多聚合物材料都具有很强的腐蚀性。使用不适用于次氯酸钠安全壳的涂料会缩短设备的使用寿命。 F010-H2O-00 Coating System for Potable Water POTABLE WATER NSF/ANSI 61 Certified Vipel F010-H2O-00 is certified to NSF/ANSI 61 for use in commercial and domestic potable water systems as a protective barrier material. If fabricators follow the ingredients and process instructions listed on page 3, they do not need to perform additional testing to manufacture a NSF/ANSI 61 compliant coating. BENEFITS Suitable for Sodium Hypochlorite Containment The formulation of Vipel F010-H2O-00 is also appropriate and suitable for sodium hypochlorite (chlorine bleach) containment. Sodium hypochlorite is a widely accepted water purification chemical that is very aggressive to most metals and many polymeric materials. The use of coatings that are not formulated for sodium hypochlorite containment will reduced the service life of the equipment. |
产品描述 Product Description
用途：管线涂料;饮用水应用;涂层应用;
性能特点： 耐碱; Alkali resistant
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
苯乙烯含量 styrene content |
39 | % | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
120 | ℃ | ASTM D648 |
|
玻璃化转变温度 Glass transition temperature |
130 | ℃ | DIN 53445 |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
表面电阻率 Surface resistivity |
> 1.0E+13 | ohms | DIN 53482 |
|
体积电阻率 Volume resistivity 2 |
> 1.0E+16 | ohms·cm | DIN 53482 |
|
介电强度 Dielectric strength |
|||
|
0.7 mm 0.7 mm |
kV/mm | DIN 53481 | |
|
介电常数 Dielectric constant |
DIN 53483 | ||
|
60 Hz 60 Hz 2 |
DIN 53483 | ||
|
60 Hz 60 Hz 3 |
DIN 53483 | ||
|
1 kHz 1 kHz 2 |
DIN 53483 | ||
|
1 kHz 1 kHz 3 |
DIN 53483 | ||
|
1 MHz 1 MHz 2 |
DIN 53483 | ||
|
1 MHz 1 MHz 3 |
DIN 53483 | ||
|
耗散因数 Dissipation factor |
DIN 53483 | ||
|
60 Hz 60 Hz 2 |
DIN 53483 | ||
|
60 Hz 60 Hz 3 |
DIN 53483 | ||
|
1 kHz 1 kHz 2 |
DIN 53483 | ||
|
1 kHz 1 kHz 3 |
DIN 53483 | ||
|
1 MHz 1 MHz 2 |
DIN 53483 | ||
|
1 MHz 1 MHz 3 |
DIN 53483 | ||
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Critical Strain Energy Critical Strain Energy |
J/m² | ASTM E399 | |
|
Gel to Peak Gel to Peak |
min | ||
|
放热峰值 exothermic peak |
℃ | ||
|
Stress Intensity Factor Stress Intensity Factor |
ASTM E399 | ||
|
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
g/cm³ | ||
|
粘度 viscosity |
|||
|
布络克菲尔德 RVT，25℃ 25℃，Brookfield RVT |
Pa·s | ||
|
胶凝时间 Gelation time |
|||
|
25℃ 25℃ |
min | ||
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
巴氏硬度 Babbitt hardness |
ASTM D2583 | ||
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D638 | |
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
MPa | ASTM D790 | |
|
压缩强度 compressive strength |
MPa | ASTM D695 | |
| 备注 |
|---|
| 1 一般属性：这些不能被视为规格。 |
| 2 after 24 hrs in drinking water |
| 3 Dry |
|
【新闻资讯】查看全部 
虾壳资料制成新型塑料袋 无望代替常规购物袋
2017-01-12 据外媒报道，近日由诺丁汉大学及埃及尼罗河大学研究人员组成的一个生物工程团队正在使用虾壳中的材料来制作一种新型塑料袋，有望代替常见的塑料购物袋。 所有不可降解的塑料袋都来自于化石燃料，而这种新型的塑料袋不仅更加环保，还能延长食品的保质期。 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付