牌号简介 About |
---|
Lexan Exl Filament AMHI240F是一款高冲击力的黑色聚碳酸酯产品。与标准聚碳酸酯相比,它在室温和极低温度下具有较高的冲击强度,并改善了UL94的性能。标称灯丝直径为1.79 mm±0.05 mm,线轴尺寸为1510 cc。 LEXAN™ EXL AMHI240F filament is a high impact polycarbonate product available in a black color. It provides high impact strength at room temperature and extreme low temperatures, in combination with improved UL94 performance over standard polycarbonate. Nominal filament diameter is 1.79 mm ± 0.05 mm and it is available in a 1510 cc spool size. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:PC Polycarbonate
用途:Additive Manufacturing (3D Printing);
加工条件:3D Printing, Fused Filament Fabrication (FFF)
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
XY 方向 XY direction |
1700 | MPa | |
XZ 方向 XZ direction |
1900 | MPa | |
ZX 方向 ZX direction |
1790 | MPa | |
拉伸强度 tensile strength 2 |
|||
XY 方向,断裂 XY direction, fracture |
45.0 | MPa | |
XZ 方向,断裂 XZ direction, fracture |
55.0 | MPa | |
ZX 方向,断裂 ZX direction, fracture |
MPa | ||
拉伸应变 Tensile strain 2 |
|||
XY 方向,断裂 XY direction, fracture |
% | ||
XZ 方向,断裂 XZ direction, fracture |
% | ||
ZX 方向,断裂 ZX direction, fracture |
% | ||
弯曲模量 Bending modulus 3 |
|||
XY 方向 XY direction |
MPa | ||
XZ 方向 XZ direction |
MPa | ||
ZX 方向 ZX direction |
MPa | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
XY 方向,-30℃ XY direction, -30 ℃ |
J/m | ||
XY 方向,23℃ XY direction, 23 ℃ |
J/m | ||
XZ 方向,-30℃ XZ direction, -30 ℃ |
J/m | ||
XZ 方向,23℃ XZ direction, 23 ℃ |
J/m | ||
ZX 方向,-30℃ ZX direction, -30 ℃ |
J/m | ||
ZX 方向,23℃ ZX direction, 23 ℃ |
J/m | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
ZX 方向:-30℃ ZX direction: -30 ℃ |
J/m | ||
XZ 方向:-30℃ XZ direction: -30 ℃ |
J/m | ||
XY 方向:-30℃ XY direction: -30 ℃ |
J/m | ||
ZX 方向:23℃ ZX direction: 23 ℃ |
J/m | ||
XZ 方向:23℃ XZ direction: 23 ℃ |
J/m | ||
XY 方向:23℃ XY direction: 23 ℃ |
J/m | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
-30℃,Total Energy -30℃,Total Energy 4 |
J | ||
-30℃,Total Energy -30℃,Total Energy 5 |
J | ||
23℃,Total Energy 23℃,Total Energy 5 |
J | ||
23℃,Total Energy 23℃,Total Energy 4 |
J | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
XY 方向:1.8 MPa,未退火,3.20 mm XY direction: 1.8 MPa, unannealed, 3.20 mm |
℃ | ||
XZ 方向:1.8 MPa,未退火,3.20 mm XZ direction: 1.8 MPa, unannealed, 3.20 mm |
℃ | ||
ZX 方向:1.8 MPa,未退火,3.20 mm ZX direction: 1.8 MPa, unannealed, 3.20 mm |
℃ | ||
维卡软化温度 Vicat Softening Temp |
|||
-- -- 5 |
℃ | ASTM D1525 6 | |
-- -- 7 |
℃ | ASTM D1525 6 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:XY 方向 MD: XY direction |
1/℃ | ||
MD:ZX 方向 MD: ZX direction |
1/℃ | ||
MD:XZ 方向 MD: XZ direction |
1/℃ | ||
TD:XY 方向 TD: XY direction |
1/℃ | ||
TD:ZX 方向 TD: ZX direction |
1/℃ | ||
TD:XZ 方向 TD: XZ direction |
1/℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
XY 方向 XY direction |
ohms·cm | ||
ZX 方向 ZX direction |
ohms·cm | ||
耗散因数 Dissipation factor |
|||
XY 方向:1.90 GHz XY direction: 1.90 GHz |
|||
ZX 方向:1.90 GHz ZX direction: 1.90 GHz |
|||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 8 |
|||
ZX 方向,3.00 mm ZX direction, 3.00 mm |
|||
XZ 方向,3.00 mm XZ direction, 3.00 mm |
|||
XY 方向,3.00 mm XY direction, 3.00 mm |
备注 |
---|
2. 类型 1, 5.0 mm/min |
3. 1.3 mm/min |
4. ZX Orientation |
5. XY Orientation |
6. 速率 A (50°C/h), 压 力1 (10N) |
7. XZ Orientation |
8. UL results provided herein may not be sufficient to waive end use part testing for UL listing. Contact UL for further details. |
【新闻资讯】查看全部
注塑模具设计时,应该留意这几种参数!
2019-03-11 注塑机上面有两个模板,一块不动,称为定模板;另外一块可以移动,称为动模板。模具就分别通过螺钉和压板固定在这两块模板上。开模时,注塑机的动模板移动,从而带动把模具打开 |
注塑模具设计时,应该留意这几种参数!
注塑机上面有两个模板,一块不动,称为定模板;另外一块可以移动,称为动模板。模具就分别通过螺钉和压板固定在这两块模板上。开模时,注塑机的动模板移动,从而带动把模具打开。
模具制造完毕,就要进行注塑成型,上注塑机,开始打产品。然而注塑机的型号很多,每种注塑机都有自己的参数。设计模具必须要能够满足客户提供的注塑机型号要求,否则将无法生产。
注塑机的设计参数很多,下面重点谈一下与模具有关的几种参数。
1.注塑量
注塑量是注塑机在生产时一次能射出熔胶的最大质量值(或容积值),代表了此种型号注塑机最大注塑能力。设计的模具一模所用的熔胶量要小于注塑机的注塑量。否则,产品打不满,无法进行生产。
2.锁模力
锁模力是注塑机在模具闭合时对模板的压紧力。被成型制品在成型时所需要的锁模力必须小于所选注塑机的额定锁模力。否则,熔胶容易从分型面处跑胶,产生飞边。
锁模力=锁模力常数×制品投影面积即:P=Kp×s
3.拉杆间距
在注塑机定模板和动模板死角有四根拉杆,他们的作用是为了保证注塑机有足够的强度和刚度,同时负责滑动模板。但它往往会限制模具的外形尺寸,因为模具安装时是从拉杆中间吊进去的。
模具外形尺寸不能同时大于他们对于的拉杆间距,如果模具的长度尺寸有一个超过了拉杆间距,则看看模具是否通过旋转吊入拉杆车间,如果旋转吊入也无法进行,那么只能更改模具尺寸,或是更换注塑机。
4.喷嘴尺寸校核
注塑机喷嘴头一般为球面,在选择浇口套的时候,应该使浇口套的球面半径与喷嘴球面半径吻合。为防止高压熔体从喷嘴与浇口套的接触间隙溢出,一般浇口套的球半径应比喷嘴求半径,同时主流道小端尺寸也应比喷嘴孔尺寸稍大,这样可使喷嘴与浇口套对位更容易。
5.定顶出装置的校核
顶出装置的分类
(1).中心顶杆机械顶出
(2).两侧双顶杆机械顶出
(3).中心顶杆液压顶出与两侧双顶杆机械顶出
(4).中心顶杆液压顶出与其他辅助油缸联合作用
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。