MFE-10是一种双酚A型环氧乙烯基酯树脂,具有低苯乙烯释放性能、适宜的粘度、优良的玻璃纤维浸润性。低苯乙烯含量,良好的耐化学性。铸件热变形温度为130°C,适用于拉挤、缠绕等热固化玻璃钢的成型工艺,用于混凝土结构材料的粘结或修补。 MFE-10 is a bisphenol-A epoxy vinyl ester resin with low styrene emission Property Suitable viscosity, excellent infiltration with glass fiber. Low styrene content Excellent chemical resistance. Heat distortion temperature of casting is 130°C Application Special for the molding processes of thermal curing FRP such as pultrusion, filament winding, etc Used to cementation or repairing material for concrete structure. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
酸值 acid value |
8.00 到 16.00 | mg KOH/g | |
固体含量 Solid content |
70 到 76 | % | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
130 | ℃ | ASTM D648 |
热稳定性 thermal stability |
|||
80℃ 80℃ |
1 | day | |
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
25℃ 25℃ |
400 到 500 | cP | |
胶凝时间 Gelation time |
|||
25℃ 25℃ |
min | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
巴氏硬度 Babbitt hardness |
ASTM D2583 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
我国数控机床开展态势及投资机遇剖析
2016-01-21 近年来,随着国防、航空、高铁、汽车和模具等重要装备制造行业需求量的大幅增长,我国数控机床也取得了快速发展,数控机床技术在高速化、复合化、精密化、多轴化等方面取得了显著进步和一系列突破。但在精度、可靠性方面和国外的数控机床还有很大差距。 目前数控机床产品中,中低端产品我国企业已有一定实力,但高档数控机床仍是短板,而高档数控机床是航空航天、汽车、船舶和发电设备制造这四大领域的必需,是产业升级的必备。尽管国家实施了“高档数控机床与基础制造装备”科技重大专项,并计划到2020年四大 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |