Technyl One J 60x1 V15黑色是一种基于非卤化阻燃系统的高温聚酰胺,用15%的玻璃纤维增强,具有一流的防火性能,用于注塑成型。与传统的高性能塑料相比,该产品具有优越的电气性能。低腐蚀性确保了加工工具的使用寿命。该产品基于高流动性矩阵,在生产率和设计自由度方面具有很强的优势。提供的数据基于实验室/实验结果。这些数据可以在工业生产后进行调整。 TECHNYL® ONE J 60X1 V15 black is a high temperature polyamide based on a non-halogenated flame retardant system, reinforced with 15% of glass fiber with best-in-class fire protection behavior, for injection moulding. This product has superior electrical performance compared to traditional high-performance plastics. Its low corrosion ensures processing tools longevity. This product, based on a high fluidity matrix, offers strong benefits in term of productivity and design freedom. The data provided are based on laboratory/experimental results. These data could be adjusted after industrial production. |
产品描述 Product Description
厂家:德国道默 DOMO
类别:PA66/6T PA 66/6T
用途:电气/电子应用领域;连接器;
加工条件:注射成型 Injection Molding
性能特点: 耐热性好; 无卤; 耐腐蚀; Heat Resistance, Good,Corrosion Resistant,Halogen free
填料:玻璃纤维 15
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.30 | g/cm³ | |
收缩率 Shrinkage rate |
|||
TD TD |
1.0 | % | |
MD MD |
0.50 | % | |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.75 | % | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
1.7 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ||
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ||
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ||
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ||
熔融温度 Melting temperature |
℃ | ||
相对温度指数 Relative temperature index |
|||
电气性能,0.75 mm Electrical performance, 0.75 mm |
℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength |
|||
0.8 mm 0.8 mm |
kV/mm | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
0.80 mm 0.80 mm |
|||
1.60 mm 1.60 mm |
|||
3.20 mm 3.20 mm |
|||
灼热丝可燃性指数 Glowing wire flammability index |
|||
0.80 mm 0.80 mm |
℃ | ||
1.6 mm 1.6 mm |
℃ | ||
3.2 mm 3.2 mm |
℃ | ||
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
0.8 mm 0.8 mm |
℃ | ||
1.6 mm 1.6 mm |
℃ | ||
3.2 mm 3.2 mm |
℃ |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
大庆石化55万吨大项目开工!预计23年投产
2022-05-07 2月28日,大庆高新区林同路以南、化工一号路以北的聚碳酸酯联合项目第一部分的桩基础正式开工,预计今年4月主体工程开始施工。该项目计划总投资60亿元,占地50公顷,预计2023年 |
大庆石化55万吨大项目开工!预计23年投产
2月28日,大庆高新区林同路以南、化工一号路以北的聚碳酸酯联合项目第一部分的桩基础正式开工,预计今年4月主体工程开始施工。该项目计划总投资60亿元,占地50公顷,预计2023年10月试运行。
项目共分两期建设。其中,一期计划投资30亿元,包括建设35万吨苯酚丙酮、20万吨双酚A 、20万吨/年纯苯3套装置。同时,配套建设公用工程设施及办公生活区。一期达产后,年预计将实现销售收入40亿元、利税15亿元。二期计划投资30亿元,建设26万吨聚碳酸酯项目,达产后年预计实现销售收入40亿元、利税13亿元。
该项目自启动建设以来得到省、市、大庆高新区大力支持。接下来该项目三大部分将于2022年内梯次开工建设以高质量建设实现项目在2023年如期达产为推动石油精深加工推动“油城”发展转型添砖加瓦! |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。