牌号简介 About |
---|
Duramide PA6GF33HI是一种玻璃纤维增强的PA6,具有冲击改性,适用于要求比标准玻璃填充的PA66或PA6高强度和改善低温冲击的应用。PA6改善了表面外观。它还包含一个易于成型的润滑剂包。下面的数据表值适用于所有颜色。 Duramide PA6GF33HI is a glass fiber reinforced PA6 with impact modification developed for applications that require high strength and improved low temperature impact over standard glass filled PA66 or PA6. PA6 offers improved surface appearance. It also contains a lubricant package for easy molding. Data sheet values below are for all colors. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
1.41 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD |
3.5 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.50 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂 fracture |
155 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
4.0 | % | ASTM D638 |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-40℃,3.2mm -40℃,3.2mm |
J/m | ||
23℃,3.2mm 23℃,3.2mm |
J/m | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
3.2 mm 3.2 mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 |
备注 |
---|
2. solid |
【新闻资讯】查看全部
国际模具制造三大主流技术
2016-06-29 近年来,国内模具制造技术迅速发展,现今已成为现代制造技术的重要组成部分。国际模协秘书长罗百辉表示,现代模具制造技术政权朝着加快信息驱动、提高制造柔性、敏捷化制造及系统化集成的方向发展,模具的CAD/CAM技术,模具的激光快速成型技术,模具的精密成形技术,模具的超精密加工技术,模具在设计中采用有限元法、边界元法进行流动、冷却、传热过程的动态模拟技术,模具的CIMS技术,已在开发的模具DNM技术以及数控技术等,几乎覆盖了所有现代制造技术。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |