牌号简介 About |
---|
Corton® 1737 HSA是一种25%的矿物填充均聚聚丙烯化合物。它是为高光泽设备/组件开发的一种非常高的流动注射成型等级,并稳定以满足130°C下2000小时的热老化要求和110°C的UL RTI等级。 Corton 1737 HSA is a 25% mineral filled homopolymer polypropylene compound. It is a very high flow injection moulding grade developed for high gloss appliance/components and stabilized to meet heat ageing requirements of 2000 hours at 130°C and a UL RTI rating of 110°C. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.08 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
41 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD:3.0 mm MD:3.0 mm |
1.1 到 1.3 | % | ASTM D955 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3mm 3mm |
24 | J/m | ASTM D256 |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
3 mm 3 mm |
380 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,3.0 mm 0.45 MPa, unannealed, 3.0 mm |
℃ | ||
1.8 MPa,未退火,3.00 mm 1.8 MPa, unannealed, 3.00 mm |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-30~30℃,3.00 mm MD:-30~30℃,3.00 mm |
1/℃ | ASTM D696 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,3.00 mm Shore D, 3.00 mm |
|||
邵氏 D,15 秒,3.00 mm Shore D, 15 seconds, 3.00 mm |
|||
洛氏硬度 Rockwell hardness |
|||
R 级,3.00 mm R-grade, 3.00 mm |
ASTM D785 | ||
拉伸强度 tensile strength 2 |
|||
3 mm 3 mm 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂,3 mm Fracture, 3 mm 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
3 mm 3 mm |
MPa | ASTM D790 |
备注 |
---|
2. 50 mm/min |