牌号简介 About |
---|
PA 6,65%矿物/玻璃纤维,注塑成型,无卤阻燃,提高流动性,尽管填充度高,优化激光标记(1064nm) Durethan® DPBM65XFM30 901510 DUS013 (Dry) PA 6, 65 % mineral/glass fibres, injection molding, halogen free flame retardant, improved flowability despite the high degree of filling, optimized for laser marking (1064nm) Durethan® DPBM65XFM30 901510 DUS013 PA 6, 65 % mineral/glass fibres, injection molding, halogen free flame retardant, improved flowability despite the high degree of filling, optimized for laser marking (1064nm) Durethan® DPBM65XFM30 901510 DUS013 PA 6, 65 % mineral/glass fibres, injection molding, halogen free flame retardant, improved flowability despite the high degree of filling, optimized for laser marking (1064nm) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.69 | g/cm³ | |
收缩率 Shrinkage rate |
|||
TD:120℃,2.0 mm TD:120℃,2.0 mm 2 |
0.10 | % | |
TD:280℃,2.0 mm TD:280℃,2.0 mm 3 |
0.50 | % | |
MD:120℃,2.0 mm MD:120℃,2.0 mm 2 |
0.10 | % | |
MD:280℃,2.0 mm MD:280℃,2.0 mm 3 |
0.40 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ||
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ||
弯曲模量 Bending modulus 4 |
|||
23℃ 23℃ 4 |
MPa | ||
弯曲强度 bending strength 4 |
|||
23℃ 23℃ 4 |
MPa | ||
弯曲应变 Bending strain 5 |
% | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
kJ/m² | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ||
维卡软化温度 Vicat Softening Temp |
℃ | ||
熔融温度 Melting temperature 6 |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23~55℃ MD:23~55℃ |
1/℃ | ||
TD:23~55℃ TD:23~55℃ |
1/℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
介电强度 Dielectric strength |
|||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.20 mm 1.20 mm |
|||
1.50 mm 1.50 mm |
|||
灼热丝可燃性指数 Glowing wire flammability index |
|||
0.80 mm 0.80 mm |
℃ | ||
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
0.8 mm 0.8 mm |
℃ | ||
极限氧指数 Extreme oxygen index 7 |
% | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
备注 |
---|
2. 60x60x2mm, 4 hr |
3. 60x60x2mm, 80°C MT, 500 bar |
4. 2.0 mm/min |
5. 2 mm/min |
6. 10°C/min |
7. 程序 A |
【新闻资讯】查看全部
Recreus推出用于3D打印的导电Filaflex TPU长丝
2021-07-22 搜料网资讯: Recreus推出Conductive Filaflex,用于3D打印的新型柔性导电TPU长丝。Conductive Filaflex是新的柔性导电TPU长丝,是制造导电零件或部件以及创造可穿戴设备的理想选择。 Recreus不断创 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |