牌号简介 About |
---|
PBT+PET,20%玻璃纤维,注塑成型,提高冲击强度,降低翘曲倾向,改善表面光洁度 POCAN® TS3220 901510 PBT+PET, 20 % glass fibers, injection molding, improved impact strength, low tendency to warp, improved surface finish POCAN® TS3220 901510 PBT+PET, 20 % glass fibers, injection molding, improved impact strength, low tendency to warp, improved surface finish POCAN® TS3220 901510 PBT+PET, 20 % glass fibers, injection molding, improved impact strength, low tendency to warp, improved surface finish |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.38 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
270℃,5 kg 270℃,5 kg |
18.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
|||
TD:120℃,2.0 mm TD:120℃,2.0 mm 2 |
0.10 | % | |
TD:270℃,2.0 mm TD:270℃,2.0 mm 3 |
0.70 | % | |
MD:120℃,2.0 mm MD:120℃,2.0 mm 2 |
0.10 | % | |
MD:270℃,2.0 mm MD:270℃,2.0 mm 3 |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus 4 |
|||
23℃ 23℃ 4 |
MPa | ISO 178-A | |
弯曲强度 bending strength 4 |
|||
23℃ 23℃ 4 |
MPa | ISO 178-A | |
弯曲应变 Bending strain 5 |
% | ISO 178/A | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B120 B120 |
℃ | ISO 306/B120 | |
熔融温度 Melting temperature 6 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23~55℃ MD:23~55℃ |
1/℃ | ||
TD:23~55℃ TD:23~55℃ |
1/℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
备注 |
---|
2. 60x60x2mm, 4 hr |
3. 60x60x2mm, 90°C MT, 600 bar |
4. 2.0 mm/min |
5. 2 mm/min |
6. 10°C/min |
【新闻资讯】查看全部
印度塑料模具行业将大展雄图
2016-12-27 在世界性和区域性贸易自由化加速发展的背景下,印度贸易自由化的进程进一步加快,这推动了进出口贸易规模的扩大,促进了产业部门尤其是制造业的出口贸易、劳动生产率和最终收入的增长。 2008年金融危机以后,印度塑料模具行业确实受到一定程度冲击,尤其是重要的消费领域如汽车模具行业需求一度低迷,但随着经济形势的好转,塑料模具行业将会强劲增长,业界的乐观情绪也愈来愈高涨。到2015年,印度塑料产量翻一番,从年产750万吨达到年产1500万吨,印度将很快成为世界第三大塑料消费国,期间塑料模 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |