牌号简介 About |
---|
LDF260YY是一种低密度聚乙烯薄膜挤出树脂,是一个赤脚级。LDF260YY符合21 CFR 177.1520(c)2.1和(c)2.2中规定的美国食品药品监督管理局(FDA)食品接触使用标准。用途:洗衣膜、纺织品包装、生产膜、尿布衬背等优点:牵伸性好,加工性能优异。 LDF260YY is a low density polyethylene resin for film extrusion and is a barefoot grade. LDF260YY meets the U.S. Food and Drug Administration (FDA) criteria for food contact use as specified in 21 CFR 177.1520 (c) 2.1 & (c) 2.2. APPLICATIONS: Laundry film, Textile packaging, Produce film, Diaper backing ADVANTAGES: Good drawdown and excellent processability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.922 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
5.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
30 | µm | |
割线模量 Secant modulus |
|||
1% 正割,MD:30 µm,吹塑薄膜 1% secant, MD: 30 µ m, blow molded film |
186 | MPa | |
1% 正割,TD:30 µm,吹塑薄膜 1% secant, TD: 30 µ m, blow molded film |
206 | MPa | |
拉伸强度 tensile strength |
|||
MD,断裂,30 µm,吹塑薄膜 MD : Break, 1.2 mil, Blown Film |
MPa | ||
TD,断裂,30 µm,吹塑薄膜 TD, fracture, 30 µ m, blow molded film |
MPa | ||
拉伸应变 Tensile strain |
|||
MD,断裂,30 µm,吹塑薄膜 MD : Break, 1.2 mil, Blown Film |
% | ||
TD,断裂,30 µm,吹塑薄膜 TD, fracture, 30 µ m, blow molded film |
% | ||
落锤冲击 Drop hammer impact |
|||
30 µm,吹塑薄膜 30 µ m, blow molded film |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD:30 µm,吹塑薄膜 MD: 30 µ m, blow molded film |
g | ||
TD:30 µm,吹塑薄膜 TD: 30 µ m, blow molded film |
g | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
国家发改委:油气价格攀升对中国影响可控
2022-03-16 近期,国际原油、天然气价格攀升。对此,国家发改委副主任连维良在上周举行的国新办新闻发布会上表示,由于中国原油、天然气外采比例较高,因此肯定会受到影响,进口成本客观 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |