牌号简介 About |
---|
0.250(6.35 mm)壁厚、10%gr.高弯曲强度和模量、抗冲击/耐热时的各种重量减轻。0.250(6.35 mm)时为V-0/5 V。 Various weight reductions at 0.250" (6.35 mm) wall, 10% GR. High flexural strength and modulus, impact/heat resistant. V-0/5V at 0.250" (6.35 mm). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- 3 |
1.12 | g/cm³ | |
-- -- |
1.25 | g/cm³ | |
收缩率 Shrinkage rate |
|||
MD:6.4 mm MD:6.4 mm |
0.40 到 0.60 | % | 内部方法 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.16 | % | |
平衡,23℃ Equilibrium, 23 ℃ |
0.32 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
6.40 mm 6.40 mm |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
|||
屈服,6.35 mm Yield, 6.35 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,6.35 mm Fracture, 6.35 mm |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
6.40 mm 6.40 mm |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服,6.40 mm Yield, 6.40 mm |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
跌落标靶冲击 Falling target impact |
|||
23℃ 23℃ |
J | 内部方法 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,6.4 mm 0.45 MPa, unannealed, 6.4 mm |
℃ | ||
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~95℃ MD:-40~95℃ |
1/℃ | ASTM E831 | |
比热 specific heat |
J/kg/℃ | ASTM C351 | |
导热系数 Thermal conductivity coefficient |
W/m/K | ASTM C177 | |
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 Electrical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电常数 Dielectric constant |
|||
100 Hz 100 Hz |
|||
1 MHz 1 MHz |
|||
耗散因数 Dissipation factor |
|||
100 Hz 100 Hz |
|||
1 MHz 1 MHz |
|||
耐电弧性 Arc resistance 4 |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
3.00 mm 3.00 mm |
UL 94 | ||
Flame Class Minimum Density(Foam) Flame Class Minimum Density(Foam) |
kg/m³ | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Weight Reduction Weight Reduction |
|||
Foam - Electrical:6.40 mm Foam - Electrical:6.40 mm |
% | ||
Foam - Impact:6.40 mm Foam - Impact:6.40 mm |
% | ||
Foam - Mechanical:6.40 mm Foam - Mechanical:6.40 mm |
% | ||
Foam - Physical:6.40 mm Foam - Physical:6.40 mm |
% | ||
Foam - Thermal:6.40 mm Foam - Thermal:6.40 mm |
% |
备注 |
---|
3. Foam Molded |
4. 钨电极 |
【新闻资讯】查看全部
中石油自主研发的极低密度聚乙烯树脂成功工业化生产
2020-11-19 搜料网资讯: 11月初,由石油化工研究院自主研发的极低密度聚乙烯热收缩膜专用料DQVL0810生产技术,在大庆石化塑料厂7.8万吨/年线性低密度聚乙烯工业装置上成功实现首次工业化应用 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |