牌号简介 About |
---|
PA 66,30%玻璃纤维,注塑成型,热老化稳定,改善表面光洁度 Durethan® AKV30GH2.0 900051 SR1 (Dry) PA 66, 30 % glass fibers, injection molding, heat-aging stabilized, improved surface finish Durethan® AKV30GH2.0 900051 SR1 PA 66, 30 % glass fibers, injection molding, heat-aging stabilized, improved surface finish Durethan® AKV30GH2.0 900051 SR1 PA 66, 30 % glass fibers, injection molding, heat-aging stabilized, improved surface finish |
产品描述 Product Description
厂家:德国朗盛 LANXESS
类别:PA66 PA66
加工条件:注射成型 Injection Molding
性能特点: 热稳定性好; 表面光泽度好; Good surface appearance,Heat Stabilized
填料:玻璃纤维 30
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.36 | g/cm³ | |
表观密度 Apparent density |
0.70 | g/cm³ | |
收缩率 Shrinkage rate |
|||
TD:120℃,3.0 mm TD:120℃,3.0 mm 2 |
0.080 | % | |
TD:290℃,3.0 mm TD:290℃,3.0 mm 3 |
0.94 | % | |
MD:120℃,3.0 mm MD:120℃,3.0 mm 2 |
0.040 | % | |
MD:290℃,3.0 mm MD:290℃,3.0 mm 3 |
% | ||
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-40℃ -40℃ |
kJ/m² | ||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
kJ/m² | ||
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
|||
-30℃,冲击总贯穿能量 -30 ℃, total impact penetration energy |
J | ||
23℃,冲击总贯穿能量 23 ℃, total impact penetration energy |
J | ||
多轴向仪器化冲击力峰值 Multi axial instrumented peak impact force |
|||
-30℃ -30℃ |
N | ||
23℃ 23℃ |
N | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ||
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ||
维卡软化温度 Vicat Softening Temp |
℃ | ||
熔融温度 Melting temperature 6 |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23~55℃ MD:23~55℃ |
1/℃ | ||
TD:23~55℃ TD:23~55℃ |
1/℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ||
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | ||
介电强度 Dielectric strength |
|||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | ||
相对电容率 Relative permittivity |
|||
23℃,100 Hz 23℃,100 Hz |
|||
23℃,1 MHz 23℃,1 MHz |
|||
耗散因数 Dissipation factor |
|||
23℃,100 Hz 23℃,100 Hz |
|||
23℃,1 MHz 23℃,1 MHz |
|||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
US FMVSS302 US FMVSS302 |
|||
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
|||
灼热丝可燃性指数 Glowing wire flammability index |
|||
2.0 mm 2.0 mm |
℃ | ||
极限氧指数 Extreme oxygen index 7 |
% | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
球压硬度 Ball hardness |
MPa | ||
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ||
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ||
弯曲模量 Bending modulus 4 |
|||
23℃ 23℃ 4 |
MPa | ||
弯曲强度 bending strength 4 |
|||
23℃ 23℃ |
MPa | ||
3.50% 应变,23℃ 3.50% strain, 23 ℃ |
MPa | ||
弯曲应变 Bending strain 5 |
% |
备注 |
---|
2. 150x105x3mm, 4 hr |
3. 150x105x3mm, 80°C MT, 500 bar |
4. 2.0 mm/min |
5. 2 mm/min |
6. 10°C/min |
7. 程序 A |
【新闻资讯】查看全部
龙佰集团拟投建2项目 推动全产业链优化升级
2021-08-07 搜料网资讯: 8月4日,龙佰集团公告称,公司控股子公司甘肃国钛拟投资建设3万吨/年转子级海绵钛技术提升改造项目,总投资18亿元,建设周期为4年。另外,全资子公司矿冶公司拟投资 |
龙佰集团拟投建2项目 推动全产业链优化升级 搜料网资讯:8月4日,龙佰集团公告称,公司控股子公司甘肃国钛拟投资建设3万吨/年转子级海绵钛技术提升改造项目,总投资18亿元,建设周期为4年。另外,全资子公司矿冶公司拟投资建设700万吨/年绿色高效选矿项目,保障公司钛矿供应,投资估算6亿元,项目建设时间为1年7个月。 龙佰集团表示,目前国产海绵钛主要集中在中低端产品市场,适用于航空航天领域的高端海绵钛是短板,在航空用海绵钛基础上要求更进一步的转子级海绵钛在中国更是稀缺产品。该项目的实施将丰富公司的钛产品系列,推动公司钛精矿—氯化钛渣—氯化法钛白粉—海绵钛—钛合金全产业链的优化升级,提升公司盈利能力与核心竞争力。 而龙佰集团全资子公司矿冶公司此次拟投资建设的700万吨/年绿色高效选矿项目,建设内容及规模包括新增处理原矿700万吨/年,新增铁精矿160万吨/年、钛精矿40万吨/年、硫钴精矿1.5万吨/年。项目建成后,公司原矿处理能力达2200万吨/年,可生产铁精矿500万吨/年、钛精矿120万吨/年、硫钴精矿5万吨/年。 龙佰集团称,该项目的实施进一步保障公司长期稳定的原料供应,既获得了高质量的铁精矿,又充分回收资源中的钛,同时回收钴等硫化物,为全面综合开发利用红格钒钛磁铁矿资源奠定基础,巩固行业优势地位。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- 电动汽车零件壳体的轻量化
- 2022-07-20 0
- Durethan® BKV 50 H3.0 000000 含有50%的玻璃纤维增强的PA 6材料,用注射成型的方式进行加工,具有良好的热老化稳定性。
- 阅读全文
电动汽车零件壳体的轻量化
1-符合冷却系统方面的要求
2-满足轻量化需求
3-拥有良好的强度与刚度
4-对冷却剂有更好的耐受性
5-优异的耐热性,能长期承受85℃的温度
6-热稳定性好
7-对水乙二醇混合物的长期耐受性好
8-爆破载荷高达10bar
2-满足轻量化需求
3-拥有良好的强度与刚度
4-对冷却剂有更好的耐受性
5-优异的耐热性,能长期承受85℃的温度
6-热稳定性好
7-对水乙二醇混合物的长期耐受性好
8-爆破载荷高达10bar
收起