牌号简介 About |
---|
特性:低粘度基本产品应用:单丝、刷毛和牙刷的高回收率。其在热变形温度(熔点高出近40°C)下的优势超过了PA 12。拉伸和弯曲强度在高湿强度下的显著回收。维斯塔的PA 612化合物因此,Mid D系列产品代表了特殊产品,是对Vestamid L系列PA 12化合物综合选择的补充。 Characterization: low-viscosity base product Applications: monofilaments, bristles with high recovery for paint brushes and tooth brushes Its advantages over PA 12 exhibit in the heat deflection temperature (melting point nearly 40 °C higher) tensile and flexural strength outstanding recovery at high wet strength The PA 612 compounds of the VESTAMID® D series consequently represent specialty products that complement the comprehensive selection of PA 12 compounds of the VESTAMID® L series. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.06 | g/cm³ | |
收缩率 Shrinkage rate 2 |
|||
TD TD |
1.0 | % | |
MD MD |
1.4 | % | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
2.6 | % | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
1.0 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ||
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ||
断裂 fracture |
% | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃,完全断裂 -30 ℃, completely fractured |
kJ/m² | ||
23℃,完全断裂 23 ℃, completely fractured |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃ -30℃ |
|||
23℃ 23℃ |
|||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ||
0.45 MPa,未退火 0.45 MPa, unannealed 3 |
℃ | ||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ||
1.8 MPa,未退火 1.8 MPa, unannealed 3 |
℃ | ||
维卡软化温度 Vicat Softening Temp |
℃ | ||
熔融温度 Melting temperature 4 |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23~55℃ MD:23~55℃ |
1/℃ | ||
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ||
介电强度 Dielectric strength |
kV/mm | ||
相对电容率 Relative permittivity |
|||
100 Hz 100 Hz |
|||
1 MHz 1 MHz |
|||
耗散因数 Dissipation factor |
|||
100 Hz 100 Hz |
|||
1 MHz 1 MHz |
|||
相比漏电起痕指数 Compared to the leakage tracing index 5 |
|||
解决方案 A Solution A 5 |
V | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
可燃性等级 Flammability level |
|||
1.6 mm 1.6 mm |
|||
3.2 mm 3.2 mm |
|||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
电解腐蚀 Electrolytic corrosion |
|||
ISO Shortname ISO Shortname |
备注 |
---|
2、specimen 127x12.7x3.2 mm processing acc. to ISO 1874-2 |
3、after conditioning at 180 °C / 60 min |
4、2nd heating |
5、50 drops Value |
【新闻资讯】查看全部
全球首套煤基MMA装置在哈密投产!远期规划70万吨
2022-09-05 扫描上图二维码,可以免费下载 搜料 APP 8月30日,新疆众友浦汇科技有限公司万吨级煤基甲醇醋酸制甲基丙烯酸甲酯生产装置,在哈密市伊吾县工业园区淖毛湖煤化工循环经济产业区稳 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |