牌号简介 About |
---|
Ryton® R-7-232NA玻璃纤维和矿物填充聚苯硫醚化合物在持续或反复暴露于高温环境中后提供增强的机械强度。Ryton® R-7-232NA适用于需要食品批准的申请,并符合现行的FDA和欧盟食品10/2011条例。 Ryton® R-7-232NA glass fiber and mineral filled polyphenylene sulfide compound provides enhanced mechanical strength after constant or repeated exposure to high temperature environments. Ryton R-7-232NA is for applications which require food approvals and is in line with current FDA and EU Food 10/2011 regulations. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.97 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.18 | % | |
TD:3.2 mm TD:3.2 mm |
0.57 | % | |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.013 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
66 | J/m | ASTM D256 |
-- -- |
kJ/m² | ISO 180-A | |
-40℃ -40℃ |
kJ/m² | ISO 180 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
3.2 mm 3.2 mm |
J/m | ASTM D4812 | |
-- -- |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
熔融温度 Melting temperature |
℃ | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-50~50℃ MD:-50~50℃ |
1/℃ | ||
MD:50~100℃ MD:50~100℃ |
1/℃ | ||
MD:120~200℃ MD:120~200℃ |
1/℃ | ||
TD:-50~50℃ TD:-50~50℃ |
1/℃ | ||
TD:50~100℃ TD:50~100℃ |
1/℃ | ||
TD:125~200℃ TD:125~200℃ |
1/℃ | ||
导热系数 Thermal conductivity coefficient |
W/m/K | ||
UL温度额定值 UL temperature rating |
℃ | UL 746B | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
25 ℃,1 kHz 25 ℃,1 kHz |
|||
25 ℃,1 MHz 25 ℃,1 MHz |
|||
耗散因数 Dissipation factor |
|||
25℃,1 kHz 25℃,1 kHz |
|||
25℃,1 MHz 25℃,1 MHz |
|||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | UL 746 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
|||
R 级 R-level |
|||
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
泊松比 Poisson's ratio |
ISO 527 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
中美海运价格“退烧”为外贸企业减压 后期价格走势判断存分歧
2021-10-11 搜料网资讯: 近期,持续上涨的海运价格似乎出现降温趋势。今年十一前,海运价格呈现小幅回落。据上海航运交易所9月30日公布的数据显示,中国出口集装箱运价指数(CCFI)为3220. |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |