牌号简介 About |
---|
sarlink FM-2265是一种通用热塑性弹性体,可用于NaT、BLK和彩色,设计用于汽车内部应用,包括地板垫。SARLINK FM-2265是一种紫外稳定、中等硬度、高密度、耐磨、填充级、加工性能优异、热稳定性好、适用于注塑成型的材料。 Sarlink FM-2265 is a general purpose thermoplastic elastomer, available in NAT, BLK, and colors, designed for automotive interior applications, including floor mats. Sarlink FM-2265 is a UV stabilized, medium hardness, high density, wear-resistant, filled grade with excellent processability, good heat stability, and suitable for injection molding. |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,1 秒,注塑成型 Shore A, 1 second, injection molding |
62 | ||
邵氏 A,5 秒,注塑成型 Shore A, 5 seconds, injection molding |
60 | ||
邵氏 A,15 秒,注塑成型 Shore A, 15 seconds, injection molding |
58 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
TD,断裂 TD, fracture |
MPa | ||
MD,断裂 MD, fracture |
MPa | ||
拉伸应变 Tensile strain 2 |
|||
TD,断裂 TD, fracture |
% | ||
流量,断裂 Flow rate, fracture |
% | ||
撕裂强度 tear strength 3 |
|||
TD TD |
kN/m | ||
MD MD |
kN/m | ||
压缩形变 Compression deformation 4 |
|||
23℃,22 hr 23℃,22 hr |
% | ||
70℃,22 hr 70℃,22 hr |
% | ||
90℃,70 hr 90℃,70 hr |
% | ||
125℃,70 hr 125℃,70 hr |
% | ||
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air 5 |
|||
TD:110℃,1008 hr TD:110℃,1008 hr |
% | ||
MD:110℃,1008 hr MD:110℃,1008 hr |
% | ||
TD:100% 应变 110℃,1008 hr TD: 100% strain at 110 ℃, 1008 hr |
% | ||
MD:100% 应变 110℃,1008 hr MD: 100% strain at 110 ℃, 1008 hr |
% | ||
TD:125℃,168 hr TD:125℃,168 hr |
% | ||
MD:125℃,168 hr MD:125℃,168 hr |
% | ||
TD:100% 应变 125℃,168 hr TD: 100% strain 125 ℃, 168 hr |
% | ||
MD:100% 应变 125℃,168 hr MD: 100% strain 125 ℃, 168 hr |
% | ||
在空气中断裂时拉伸应力变化 Changes in tensile stress during fracture in air 5 |
|||
TD:110℃,1008 hr TD:110℃,1008 hr |
% | ||
流量:110℃,1008 hr Flow rate: 110 ℃, 1008 hr |
% | ||
TD:125℃,168 hr TD:125℃,168 hr |
% | ||
流量:125℃,168 hr Flow rate: 125 ℃, 168 hr |
% | ||
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
|||
邵氏 A,110℃,1008 hr Shore A, 110 ℃, 1008 hr 6 |
|||
邵氏 A,110℃,1008 hr Shore A, 110 ℃, 1008 hr 7 |
|||
邵氏 A,110℃,1008 hr Shore A, 110 ℃, 1008 hr 8 |
|||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr 6 |
|||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr 7 |
|||
邵氏 A,125℃,168 hr Shaw A, 125 ℃, 168 hr 8 |
|||
法律声明 Legal Statement |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
|||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
g/10min | ASTM D1238 | |
熔体表观粘度 Apparent viscosity of melt |
|||
200℃,206 sec^-1 200℃,206 sec^-1 |
Pa·s | ASTM D3835 | |
特殊值 |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
TD,100% 应变 TD, 100% strain |
1.35 | MPa | |
MD,100% 应变 MD, 100% strain |
1.97 | MPa |
备注 |
---|
2、类型 1, 510 mm/min |
3、B 方法,直角形试样(不割口), 510 mm/min |
4、类型 A |
5、类型 1 |
6、15 sec |
7、5 sec |
8、1 sec |
【新闻资讯】查看全部
搜料网告诉你聚碳酸酯PC 4、5月份会不会继续掉价
2018-03-29 进入3月中下旬,由于鲁西抛出26含税千吨甩货计划,直接导致了国内PC市场恐慌性的雪崩,半个月之内: 乐天1100从不含税26/kg掉到24,科思创2805从不含税28/kg掉到26 ,大风02-10从开年的含税 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名:搜料网-Sarlink® TPE FM-2265 (PRELIMINARY DATA)证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)