特点和优点组成:偏氟乙烯、六氟丙烯和四氟乙烯三元共聚物低氟版Fe5830Q工艺目标:仅挤出,不推荐用于模制品应用专有的复合固化技术可在不使用加工助剂的情况下生产出光滑的挤出物。为了满足-40°C的芯轴弯曲燃料软管规格,可制定出对汽车燃料具有良好的渗透性的软管规格。 Features and Benefits Composition: terpolymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethylene Lower fluorine version of FE 5830Q Process targets: extrusion only, not recommended for molded goods applications Proprietary incorporated cure technology Produces smooth extrudates without the use of processing aids Can be formulated to meet -40°C mandrel bend fuel hose specifications Can be formulated to yield good permeation resistance to automotive fuels |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.87 | g/cm³ | |
门尼粘度 Mooney viscosity |
|||
ML 1+10,121℃ ML 1+10,121℃ |
36 | MU | |
氟含量 Fluorine content |
69 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
71 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
10.1 | MPa | |
100% 应变 100% strain |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ||
压缩形变 Compression deformation |
|||
200℃,70 hr 200℃,70 hr |
% | ASTM D395B | |
MH(177℃) MH(177℃) |
J | ||
ML(177℃) ML(177℃) |
J | ||
t'50(177℃) t'50(177℃) |
min | ||
t'90(177℃) t'90(177℃) |
min | ||
ts2(177℃) ts2(177℃) |
min | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Tr10 Tr10 |
℃ | ASTM D1329 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
先正达集团一季度营收71亿美元 同比增长20%
2021-05-03 搜料网资讯: 4月29日,先正达集团宣布2021年第一季度业绩强劲。第一季度营业收入71亿美元,比2020年第一季度增长20%。以固定汇率(C ER )增长18%。第一季度EBITDA增长19%(按CER计增 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |