牌号简介 About |
---|
EPOXACAST 650和EPOXACAST 650黑色为矿物填充通用铸造环氧树脂,成本低,用途广泛。它们的特点是混合粘度低,气泡截留最小。选择快速、中等或缓慢的Catalyst以适合您的项目。你也可以使用高温硬化剂来提高铸件的耐热性。epoxacast 650和epoxacast 650黑色用于制造金属冲压的硬质模具以及图案和夹具。它们还用于电气封装,以延长使用寿命,提高封装电子设备的性能。EPOXACAST 650和EPOXACAST 650黑色的高抗压强度使其成为制作金属饰品冲压模具的理想选择。 EpoxAcast® 650 and EpoxAcast® 650 BLACK are mineral filled general purpose casting epoxies that are low cost and versatile. They feature a low mixed viscosity for minimal bubble entrapment. Choose Fast, Medium or Slow catalyst to fit your project. You can also use HT Hardener to give your castings higher heat resistance. EpoxAcast® 650 and EpoxAcast® 650 BLACK are used for making hard dies for metal stamping as well as patterns and fixtures. They are also used for electrical encapsulation to extend the life cycles and enhance the performance of potted electronic devices. The high compressive strength of EpoxAcast® 650 and EpoxAcast® 650 BLACK makes it ideal for making stamping dies for production pressing of metal ornaments. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.52 | g/cm³ | ASTM D1475 |
特定体积 Specific volume |
0.658 | cm³/g | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD MD 2 |
0.10 | % | |
MD MD 3 |
0.70 | % | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
|||
23℃ 23℃ 5 |
1.0 | hr | |
23℃ 23℃ 6 |
hr | ||
23℃ 23℃ 9 |
hr | ||
66℃ 66℃ 5 |
hr | ||
66℃ 66℃ 6 |
hr | ||
66℃ 66℃ 7 |
hr | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
巴氏硬度 Babbitt hardness |
ASTM D2240 | ||
拉伸模量 Tensile modulus |
|||
-- -- 3 |
MPa | ||
-- -- 2 |
MPa | ||
拉伸强度 tensile strength |
|||
断裂 fracture 3 |
MPa | ||
断裂 fracture 2 |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂 fracture 2 |
% | ||
断裂 fracture 3 |
% | ||
弯曲模量 Bending modulus |
|||
-- -- 3 |
MPa | ||
-- -- 2 |
MPa | ||
弯曲强度 bending strength |
|||
-- -- 2 |
MPa | ||
-- -- 3 |
MPa | ||
压缩模量 Compression modulus |
|||
-- -- 3 |
MPa | ||
-- -- 2 |
MPa | ||
压缩强度 compressive strength |
|||
-- -- 2 |
MPa | ||
-- -- 3 |
MPa | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
-- -- 2 |
℃ | ||
-- -- 4 |
℃ | ||
热固组件 Thermosetting components |
|||
部件 A Component A 7 |
|||
部件 B Component B 5 |
|||
部件 B Component B 6 |
|||
部件 B Component B 7 |
|||
部件 B Component B 8 |
|||
储存稳定性 storage stability |
|||
23℃ 23℃ 5 |
min | ||
23℃ 23℃ 6 |
min | ||
23℃ 23℃ 7 |
min | ||
23℃ 23℃ 8 |
min | ||
热固性混合粘度 Thermosetting mixed viscosity |
|||
-- -- 2 |
cP | ||
-- -- 3 |
cP |
备注 |
---|
2、Using 101, 102 or 103 Hardener |
3、Using HT Hardener |
4、Using HT Hardener, Post cured |
5、101 FAST Hardener |
6、102 MEDIUM Hardener |
7、103 SLOW Hardener |
8、HT HIGH TEMP Hardener |
9、HT HIGH TEMP Hardener, followed by 2 hr at 175°F and 3 hr at 300°F |
【新闻资讯】查看全部
奇葩资料:把宇航员的尿液变成塑料
2017-08-23 太空飞行是神奇的,但大家有否想过,人类在太空上制造的垃圾,最终会以怎样的方式处理?克莱姆森大学的科学家提出了一个解决方案:将宇航员的废弃物转化成可以投入到3D打印机 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |