| 牌号简介 About |
|---|
| Lupoy PC 1301EP-30树脂专为挤出和注塑产品设计。它在耐热性、透明度和冲击强度方面表现出良好的物理性能平衡。主要特点极低粘度好的脱模应用DVD保险盒手机键盘包装应用薄组件 LUPOY PC 1301EP-30 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength. Main Characteristics Very low viscosity Good mold release Applications DVD security boxes Mobile phone keypads Packaging applications Thin components |
产品描述 Product Description
用途：包装;薄壁部件;
加工条件：挤出 Extrusion
性能特点： 耐热性好; 含脱模剂; 透光性好; 低粘度; 冲击性能好; Good Clarity,High impact resistance,Low Viscosity,Good stripping performance,Heat Resistance, Good
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.20 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
300℃，1.20kg 300℃，1.20kg |
30 | g/10min | ASTM D1238 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.50 到 0.70 | % | ASTM D955 |
|
吸水率 Water absorption rate |
|||
|
23℃，24hr 23℃，24hr |
0.15 | % | |
|
平衡，23℃，50% RH Equilibrium, 23 ℃, 50% RH |
0.32 | % | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
|||
|
屈服，23℃ Yield, 23 ℃ 2 |
MPa | ||
|
断裂 fracture |
MPa | ||
|
拉伸应变 Tensile strain |
|||
|
屈服 yield |
% | ||
|
断裂 fracture |
% | ||
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
MPa | ASTM D790 | |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 3 |
|||
|
23℃，3.2mm 23℃，3.2mm 3 |
J/m | ASTM D256 | |
|
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
|
23℃ 23℃ |
ASTM D256 | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
0.45 MPa，退火，4.0 mm 0.45 MPa, annealed, 4.0 mm |
℃ | ||
|
1.8 MPa，未退火，4.0 mm 1.8 MPa, unannealed, 4.0 mm |
℃ | ||
|
1.8 MPa，退火，4.0 mm 1.8 MPa, annealed, 4.0 mm |
℃ | ||
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 4 | |
|
球压温度 Ball pressure temperature |
℃ | IEC 60598-1 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：-40~82℃ MD：-40~82℃ |
1/℃ | ASTM D696 | |
|
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
体积电阻率 Volume resistivity |
|||
|
23℃ 23℃ |
ohms·cm | ASTM D257 | |
|
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
|
介电常数 Dielectric constant |
|||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
耗散因数 Dissipation factor |
|||
|
60 Hz 60 Hz |
ASTM D150 | ||
|
相比漏电起痕指数 Compared to the leakage tracing index |
|||
|
2.00 mm 2.00 mm |
V | IEC 60112 | |
|
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
阻燃等级 Flame retardant level |
|||
|
0.50 mm 0.50 mm |
|||
|
1.60 mm 1.60 mm |
|||
|
2.50 mm 2.50 mm |
|||
|
3.00 mm 3.00 mm |
|||
|
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
|
2 mm，5.0 sec 2 mm，5.0 sec |
℃ | IEC 60695-2-13 | |
|
极限氧指数 Extreme oxygen index |
% | ASTM D2863 | |
|
平均燃烧程度 Average combustion degree |
cm | ASTM D635 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
折射率 Refractive index |
ASTM D542 | ||
|
透光率 Transmittance |
% | ASTM D1003 | |
|
雾度 Haze |
% | ASTM D1003 | |
| 备注 |
|---|
| 2、50 mm/min |
| 3、0.25 mm 缺口深度 |
| 4、速率 A (50°C/h), 载荷2 (50N) |
|
【新闻资讯】查看全部 
布拉斯科计划进行PE装置改造
2022-04-26 近日，巴西布拉斯科与墨西哥Idesa集团合资企业Braskem Idesa副首席执行官贝尔纳多阿尔瓦雷斯表示，该公司正着手其位于墨西哥的2.5万吨/年聚乙烯(PE)脱瓶颈改造项目，以及其乙烷进口终 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付