| 牌号简介 About |
|---|
| ACRYMID® 813化合物是一种基于聚甲基丙烯酸甲酯（PMMI）的无定形和耐热热塑性成型化合物。Acrymid耐热模塑料的典型性能是：高透光性、高耐热性、高强度和刚性、良好的耐候性。ACRYMID® 813化合物的特殊性能是：高熔体流动速率Ameca列出的应用：用于涉及高热应力的注塑件。 ACRYMID 813 compound is an amorphous and heat-resistant thermoplastic molding compound based on polymethyl methacrylimide (PMMI). Typical properties of ACRYMID® heat-resistant molding compounds are: high light transmission high heat resistance very high strength and rigidity good weather resistance The special properties of ACRYMID 813 compound are: high melt flow rate AMECA listed Application: Used for injection molding parts that involve a high degree of thermal stress. |
产品描述 Product Description
用途：镜头;照明装置;光纤电缆;
加工条件：注射成型 Injection Molding
性能特点： 机械强度好; 耐高温; 无定形的; 透光性好; 流动性高; 耐候抗UV; Good Rigidity,Weather resistance is good,Good Clarity,High liquidity,High Heat Resistance,Amorphous
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.21 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
260℃，3.80kg 260℃，3.80kg |
16 | g/10min | ASTM D1238 |
|
收缩率 Shrinkage rate |
|||
|
MD MD |
0.80 到 0.90 | % | ASTM D955 |
|
吸水率 Water absorption rate |
|||
|
平衡 balance |
< 0.30 | % | ASTM D570 |
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
|
23℃，6.4mm 23℃，6.4mm |
13 | J/m | ASTM D256 |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，退火，6.35 mm 1.8 MPa, annealed, 6.35 mm |
℃ | ASTM D648 | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
|
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
|
MD：0~100℃ MD：0~100℃ |
1/℃ | ASTM D696 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
透光率 Transmittance |
|||
|
3200 µm 3200 µm |
% | ASTM D1003 | |
|
雾度 Haze |
|||
|
3200 µm 3200 µm |
% | ASTM D1003 | |
|
黄度指数 Yellowness index |
|||
|
3.20 mm 3.20 mm |
YI | ASTM D1925 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
洛氏硬度 Rockwell hardness |
|||
|
M 级 M-level |
ASTM D785 | ||
|
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
|
拉伸强度 tensile strength |
MPa | ASTM D638 | |
|
拉伸应变 Tensile strain |
|||
|
屈服 yield |
% | ||
|
断裂 fracture |
% | ||
|
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
|
弯曲强度 bending strength |
MPa | ASTM D790 | |
| 备注 | |||
|---|---|---|---|
| 暂无数据 | |||
|
【新闻资讯】查看全部
巴斯夫公司有意投资伊朗最近开放的动力行业
2017-02-28 巴斯夫公司(BASF AG, BF)正在探索进入最近开放的伊朗能源市场的选项，从而成为众多期望拓展伊朗市场的德国公司中的一个。 该公司首席执行长Kurt Bock周五称，在受到伊朗当局的邀请后，该公司目前正通过其全资拥有的油气子公司Wintershall AG在伊朗探索商业机会。 Bock称，该公司正尝试观察是否有机会在伊朗油气行业获得一席之地。他称，该公司受到了伊朗政府的邀请并将进行一番考察。 作为伊朗和世界主要大国达成的核协议的一部分，去 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付