自由形式塑造是一种两部分可雕刻环氧粘土,不需要燃烧,将在短时间内自我固化到一个极其坚硬和耐用的状态,几乎没有收缩。雕刻比同类产品轻30%,更好地保持垂直表面。用户可以雕刻更大,更强壮的作品,对重量分布有更多的控制。自由形式雕刻有一个超精细的粒度,让用户能够雕刻更精细的细节,更好的精度使用工具或手工塑造。一个镜面般的,光泽的完成可以通过在它治愈之前用水平滑雕刻。最大的可用性-只需加水;当混合A+B组分时,可以通过加水来改变自由造型的一致性和可操作性。在雕刻时,可以用水使腻子表面光滑。A部分和B部分手工等量混合。工作时间很长,1.5小时,自由造型造型,一夜之间固化成坚硬、坚硬的环氧树脂,非常坚固和防水。雕刻很容易通过添加如此强烈的色彩来创造大理石或其他效果。固化后的腻子很容易用丙烯酸漆上漆。自由形态雕塑不含晶体二氧化硅(这是一种已知的致癌物)。它可以安全地用砂纸打磨、成形和上漆。作为一种修复粘合剂,自由形式的雕刻将结合到自己和各种表面,包括木材,金属,玻璃,石头和混凝土。自由形态的雕塑甚至可以在水下固化。 Free Form® SCULPT is a two part sculpt-able epoxy clay that requires no firing and will self-cure in a short time to an extremely hard and durable state with virtually no shrinkage. SCULPT is 30% lighter than similar products and holds vertical surfaces better. Users can sculpt larger, stronger pieces with more control over weight distribution. Free Form SCULPT has an ultra fine particle size that gives the user the ability to sculpt finer detail with better precision using tools or shaping by hand. A mirror-like, gloss finish can be achieved by smoothing SCULPT with water before it cures. Maximum Usability - Just Add Water; you can change the consistency and workability of Free Form® SCULPT by adding water when mixing A+B components. Putty surface can be smoothed with water while sculpting. Parts A & B are mixed in equal amounts by hand. Working time is a long 1.5 hours and Free Form® SCULPT cures overnight to a hard, rigid epoxy that is very strong and waterproof. SCULPT is easily colored by adding SO-Strong color tints to create marble or other effects. Cured putty is easily painted with acrylic paints. Free Form® SCULPT does not contain crystalline silica (which is a known carcinogen). It can be safely sanded, shaped, and painted. Used as a repair adhesive, Free Form® SCULPT will bond to itself and a variety of surfaces including wood, metal, glass, stone, and concrete. Free Form® SCULPT will even cure under water. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.33 | g/cm³ | ASTM D1475 |
特定体积 Specific volume |
0.749 | cm³/g | ASTM D1475 |
收缩率 Shrinkage rate |
|||
MD MD |
1.0 | % | ASTM D2566 |
粘度 viscosity |
Putty | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
80 | ASTM D2240 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
固化时间 Curing time |
day | ||
混合比 Mixing ratio |
|||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
储存稳定性 storage stability 2 |
min |
备注 |
---|
2、@ 1 lb./0.5 kg. mass |
【新闻资讯】查看全部
“吹塑法 ”和“流延法”工艺比拟
2016-12-22 薄膜生产领域中,“吹塑法”与“流延法”是较为常用的两种工艺,下面就这两种薄膜生产中最常用的生产工艺做一个简单的介绍与比较。 多层共挤吹塑法 这种生产工艺方法主要分为上吹风冷和下吹水冷两种形式。 上吹风冷 主要是由多台挤出机,多层叠加模头,多风口风环,IBC内冷系统,人字夹板,旋转牵引系统,下牵引系统以及收卷系统这几个主要部分组成。目前,进口机组以原德国巴登菲尔德,德国W&H,加拿大宾顿为主,国产机组中以广东金明为代表。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |