牌号简介 About |
---|
BCC PTMEG系列高性能双组分MDI弹性体经高温处理和固化后,可获得标准热铸预聚物的性能。当与BC 8590A异氰酸盐一起使用时,PTMEG系列固化至60-95邵尔A硬度范围,使机械测试值远高于标准室温系统。 BCC PTMEG series of high performance two-component MDI elastomers when processed and cured at elevated temperatures can give you the performance of a standard hot-cast prepolymer. The PTMEG series, when used with BC 8590A isocyante, cures to a range of hardness from 60-95 Shore A, giving mechanical testing values far above standard room temperature systems. |
技术参数 Technical Data | |||
---|---|---|---|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
后固化时间 Post curing time |
|||
79℃ 79℃ |
16 | hr | |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
重量混合比(PBW) Weight Mix Ratio (PBW) |
|||
Part A Part A |
100 | ||
Part B Part B |
70 | ||
胶凝时间 Gelation time |
7.0 到 10 | min | |
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
92 到 98 | ||
拉伸断裂强度 Tensile fracture strength |
MPa | ||
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ||
撕裂强度 tear strength |
|||
-- -- 2 |
kN/m | ||
Die C Die C |
kN/m |
备注 |
---|
2、Split |
【新闻资讯】查看全部
我乙烯多相氢甲酰化技术国际领先
2022-05-17 5月14日,由中国科学院大连化学物理研究所开发的5万吨/年乙烯多相氢甲酰化及其加氢制正丙醇工业化技术,通过了由中国石油和化学工业联合会组织的科技成果鉴定。鉴定委员会一致 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |