牌号简介 About |
---|
MVR(300°C/1.2 kg)6.0 cm³/10 min;15%玻璃纤维增强;UL 94V-0/3.0 mm;高粘度;易脱模;注塑-熔融温度310-330°C;挤出;仅提供不透明颜色;电动工具外壳 MVR (300 °C/1.2 kg) 6.0 cm³/10 min; 15 % glass fiber reinforced; UL 94V-0/3.0 mm; high viscosity; easy release; injection molding - melt temperature 310 - 330 °C; extrusion; available in opaque colors only; housings for power tools |
产品描述 Product Description
厂家:德国科思创 Covestro
类别:PC Polycarbonate
用途:动力/其它工具;外壳;
颜色:不透明,可用颜色
加工条件:注射成型 Injection Molding
性能特点: 防火阻燃等级V-0; 含脱模剂; 高粘度; 防火阻燃等级V-2; High Viscosity,Good stripping performance,V-2,V-0
填料:玻璃纤维 15
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.29 | g/cm³ | ISO 1183 |
表观密度 Apparent density 2 |
0.64 | g/cm³ | ISO 60 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
7.0 | g/10min | ISO 1133 |
熔体体积流动速率 Melt Volume Rate |
|||
300℃,1.2 kg 300℃,1.2 kg |
6.00 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate 3 |
ISO 294-4 | ||
TD:2.0 mm TD:2.0 mm |
0.45 | % | ISO 294-4 |
MD:2.0 mm MD:2.0 mm |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 6 |
|||
23℃,完全断裂 23 ℃, completely fractured 6 |
kJ/m² | ISO 7391 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-60℃,完全断裂 -60 ℃, completely fractured |
kJ/m² | ISO 179/1eU | |
-30℃,完全断裂 -30 ℃, completely fractured |
kJ/m² | ISO 179/1eU | |
23℃,完全断裂 23 ℃, completely fractured |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 7 |
|||
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
ISO 6603-2 | ||
-30℃ -30℃ |
J | ISO 6603-2 | |
23℃ 23℃ |
J | ISO 6603-2 | |
多轴向仪器化冲击力峰值 Multi axial instrumented peak impact force |
ISO 6603-2 | ||
-30℃ -30℃ |
N | ISO 6603-2 | |
23℃ 23℃ |
N | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
球压测试 Ball pressure test |
|||
136℃ 136℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
相对温度指数 Relative temperature index |
|||
电气性能,1.50 mm Electrical performance, 1.50 mm |
℃ | UL 746 | |
强度机械性能,1.50 mm Strength mechanical performance, 1.50 mm |
℃ | UL 746 | |
冲击机械性能,1.50 mm Impact mechanical performance, 1.50 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
IEC 60112 | ||
解决方案 A Solution A |
V | IEC 60112 | |
解决方案 B Solution B |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
极限氧指数 Extreme oxygen index 8 |
% | ISO 4589-2 | |
燃烧速率 Burning rate |
|||
USFMVSS,> 1.00 mm USFMVSS,> 1.00 mm |
ISO 3795 | ||
Flash Ignition Temperature Flash Ignition Temperature |
℃ | ASTM D1929 | |
针焰测试 Needle flame test |
IEC 60695-11-5 | ||
Method F:1.50 mm Method F:1.50 mm |
min | IEC 60695-11-5 | |
Method F:2.00 mm Method F:2.00 mm |
min | IEC 60695-11-5 | |
Method F:3.00 mm Method F:3.00 mm |
min | IEC 60695-11-5 | |
Method K:1.50 mm Method K:1.50 mm |
min | IEC 60695-11-5 | |
Method K:2.00 mm Method K:2.00 mm |
min | IEC 60695-11-5 | |
Method K:3.00 mm Method K:3.00 mm |
min | IEC 60695-11-5 | |
自燃温度 Autoignition temperature |
℃ | ASTM D1929 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
电解腐蚀 Electrolytic corrosion |
|||
23℃ 23℃ |
IEC 60426 | ||
ISO Shortname ISO Shortname |
|||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/5 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/5 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus 4 |
|||
23℃ 23℃ 4 |
MPa | ISO 178 | |
弯曲强度 bending strength 4 |
ISO 178 | ||
3.50% 应变,23℃ 3.50% strain, 23 ℃ |
MPa | ISO 178 | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲应变 Bending strain 5 |
% | ISO 178 | |
球压硬度 Ball hardness |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Pellets |
3 60x60x2 mm, 500 bar |
4 0.079 in/min |
5 2 mm/min |
6 Based on ISO 179-1eA, 3 mm |
7 Based on ISO 180-A, 3 mm |
8 程序 A |
【新闻资讯】查看全部
我国塑料机械行业需不时增强创新 与世界接轨
2017-09-14 我国塑料机械产品的市场在塑料加工领域,而我国在这一领域的企业规模普遍较小,产能过于分散,产业集中度不高,造成市场低水平竞争。 有相当部分的企业只生产基本没有技术含量的日用塑料制品和简单的工业用品,并且依靠 |
我国塑料机械行业需不时增强创新 与世界接轨 在我国塑料机械商品的市场在塑料造粒领域,而在我国在这里一领域的企业经营规模广泛较小,生产能力过度分散化,产业市场集中度不高,导致市场适度性市场竞争。 有非常一部分的企业只生产制造基础沒有技术含量的日用塑胶制品和简易的化工用品,而且借助人力资本低成本的优点,以廉价进到市场。这样一来,绝大多数中下游产品企业欠缺应用高新技术塑料机械提升商品级别的工作能力,只考虑于一般的生产加工。因为中下游企业沒有要求,塑料机械生产制造企业的技术革新难以获得市场回复,技术革新的不理智遭受非常大抑止。 现阶段塑料机械技术性在节能环保、可持续发展观的科学研究上,在我国与资本主义国家处在同一起跑点,差别不显著,中国企业能够 从该领域下手,为此为突破口,发展高档市场,凭着高技术含量的商品更改在我国塑料机械产业大而不强的局势,提高在国际性市场的竞争能力。 要使在我国的塑料机械水准尽早与全球对接,单纯性地靠引入海外技术性是不足的,务必从前沿科技的自主研发下手,更改在我国塑料机械水准的落伍局势,针对技术含量很高的塑料机械产业领域而言,要想在药业领域得到稳步发展,占有有益影响力,只有智能科技方能制胜。 来源于:环球塑化网 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。