| 牌号简介 About |
|---|
| ADVANCENE™ EE-4811-AAH高密度聚乙烯树脂是一种高分子量、高密度聚乙烯共聚物，专门设计用于管状薄膜挤出。其广泛的分子量分布和密度成功地将高挤出率下的优异性能与高薄膜强度和刚性结合起来。高强度食品袋推荐使用ADVANCENE™ EE-4811-AAH-27树脂的管状薄膜。购物袋、概念和女帽包。该产品具有优异的降膜性能，可生产用于多壁袋衬的高品质薄膜，并可替代薄纸产品。强度和降深的结合使得这种树脂在许多应用中非常适合于降深测量。胶片易于处理和打印，以获得高质量的图形。渐新世EE-4011-AAH树脂与颜色浓缩物相容，因此可以生产各种彩色薄膜，用作保护和吸引人的装饰膜。主要特点：己烯高密度树脂。高薄膜强度。良好的可加工性和收缩性。 ADVANCENE™ EE-4811-AAH High Density Polyethylene Resin is a high molecular weight, high-density polyethylene copolymer that has been designed specically for tubular film extrusion. Its broad molecular weight distribution and density successfully combine excellent performance at high extrusion rates with high film strength and rigidity. Tubular films of ADVANCENE™ EE-4811-AAH Resin are recommended for high strength grocery sacks. shopping bags and notion and millinery bags. The excellent drawdown characteristic of this product permits production of high-quality thin films for multiwall sack liners and replacements for thin paper products. The combination of strength and drawdown makes this resin ideal for downgauging in many applications. Films are readily treated and printed to give high-quality graphics. ADVANCENE™ EE-4011-AAH Resin is compatible with color concentrates, thus permitting the production of a variety of colored films that serve as protective and attractive decorative wraps. Main Characteristics: Hexene High Density Resin. High film strength. Excellent processability and drawdown. |
产品描述 Product Description
用途：薄膜;衬里;袋子;
加工条件：薄膜挤出 Film extrusion
性能特点： 可回收; 机械强度好; 印刷性好; 高密度; 共聚物; 着色性好; 宽分子量分布; 高分子量; 易剥离; 己烯共聚单体; 易加工; Good Rigidity,Excellent Processability,Good dissection,Wide molecular weight distribution,Renewable resources,Good Printability,High molecular weight,Copolymer,High density,Hexene copolymers,Good coloring
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.948 | g/cm³ | ASTM D792 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，21.6kg 190℃，21.6kg |
11 | g/10min | ASTM D1238 |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
弯曲模量 Bending modulus |
|||
|
1% 正割 1% secant |
814 | MPa | ASTM D790 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
13 | µm | |
|
膜刺穿强度 Membrane puncture strength 2 |
1.20 | J | |
|
拉伸强度 tensile strength |
|||
|
MD，屈服，13 µm MD, yield, 13 µ m |
MPa | ||
|
TD，屈服，13 µm TD, yield, 13 µ m |
MPa | ||
|
MD，断裂，13 µm MD, fracture, 13 µ m |
MPa | ||
|
TD，断裂，13 µm TD, fracture, 13 µ m |
MPa | ||
|
拉伸应变 Tensile strain |
|||
|
MD，断裂，13 µm MD, fracture, 13 µ m |
% | ||
|
TD，断裂，13 µm TD, fracture, 13 µ m |
% | ||
|
落锤冲击 Drop hammer impact |
|||
|
13 µm 13 µm |
g | ASTM D1709-A | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
|
MD：13 µm MD：13 µm 3 |
g | ||
|
TD：13 µm TD：13 µm |
g | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
|
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
| 备注 |
|---|
| 2、Univation Method |
| 3、Method B |
|
【新闻资讯】查看全部 
大连商品交易所20日PVC行情表
2022-04-20 大连商品交易所 日行情表 查询日期： 20 22 年 04 月 20 日 本月第 12 个交易日 本年第 70 个交易日 商品 交割月份 开盘价 最高价 最低价 收盘价 前结算价 结算价 涨跌 涨跌 1 成交量 持仓 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |