牌号简介 About |
---|
3M Dyneon PFE 60Z是一种技术先进的过氧化物固化全氟橡胶,旨在满足密封应用的挑战。它的全氟化主干结构提供了非常广泛的化学和热稳定性。低粘度提供良好的模具流动性,是成型大型零件的理想选择。根据ASTM D1418,它被归类为FFKM。特点和优点改进了模具流程和编织超过3M Dyneon PFE 80Z和PFE 90Z,是湿化学、流体处理、清洁和化学蚀刻工艺的理想选择,对大型零件也适用于CPI和航空航天,具有良好的耐压缩永久变形性,使用温度高达220°C,金属离子含量低,可在各种化学品中提取低。当使用PFE 80Z或PFE 90Z时,可用于调节门尼。 3M™ Dyneon™ PFE 60Z is a technically advanced peroxide curable perfluoroelastomer, designed to meet the challenges of demanding sealing applications. Its fully fluorinated backbone structure provides a very broad chemical and thermal stability. Low viscosity provides good mold flow and is ideal for molding large parts. It is classified as FFKM per ASTM D1418. Features and Benefits Improved mold flow and knitting over 3M™ Dyneon™ PFE 80Z and PFE 90Z Ideal for wet chemical, fluid handling, cleaning and chemical etching processes, and for large parts for CPI and aerospace Good compression set resistance Upper use temperature of 220°C Low metal ion content with low extractables in a wide range of chemicals Can be utilized to adjust Mooney when using PFE 80Z or PFE 90Z |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
2.00 | g/cm³ | |
门尼粘度 Mooney viscosity |
|||
ML 1+10,121℃ ML 1+10,121℃ |
60 | MU | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
75 | ASTM D2240 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
17.9 | MPa | ASTM D412 |
100% 应变 100% strain |
11.0 | MPa | ASTM D412 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
压缩形变 Compression deformation |
|||
200℃,70 hr 200℃,70 hr |
% | ||
200℃,168 hr 200℃,168 hr |
% | ||
230℃,70 hr 230℃,70 hr |
% | ||
230℃,168 hr 230℃,168 hr |
% | ||
MH MH |
J | ||
ML ML |
J | ||
t'50 t'50 |
sec | ||
t'90 t'90 |
min | ||
ts2 ts2 |
sec | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Tr10 Tr10 |
℃ |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
5种废塑料分选技术谁更优?等待你的拙见!
2017-12-19 混合的废塑料很难回收再利用或者再利用价值不高,废塑料必须分类才能达到有效回收利用的目的。塑料的分选技术很多,主要有振动分选、气流分选、液体分选、电磁分选和光电分选等技术。 1、振动分选技术 振动分选技术是利用振动床的往复运动,带动床面上的物料产生振动作用。主要原理是利用物料与床面之间产生的摩擦力及惯性力,形成物料颗粒的不同位移运动,并通过物料颗粒间的位移差达到分离的效果。振动分选在处理密度相差较大的材料分选时效果啊较好。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名:搜料网-3M™ Dyneon™ Perfluoroelastomer PFE 60Z证书
发送至:(多个地址,中间以逗号隔开)
发送一份副本给我:您还没有填写邮箱!(点击完善资料)