牌号简介 About |
---|
Solanyl® C2101是一种适合挤压的端部化合物。Solanyl® C2101可以在传统的挤压生产线上加工。Solanyl® C2101是目前使用的可生物降解塑料的竞争性替代品,如广泛应用的低密度聚乙烯。Solanyl® C2101特别适用于(多层)柔性产品。Solanyl C2191可与大多数生物聚酯或淀粉基塑料混合,以降低成本。Solanyl® C2101拥有自然的感觉和外观。Solanyl® C2101可生物降解,生物基或植物基含量大于40%。应用领域包括:消费品、包装和农产品热成型应用领域:杯子、盒子和托盘、板材(外层)以及管道挤压柔性型材等底层应用的内层。 Solanyl® C2101 is an end compound suitable for extrusion. Solanyl® C2101 can be processed on conventional extrusion lines. Solanyl® C2101 is a competitive alternative for currently used biodegradable plastics, like LDPE for a wide range of applications. Solanyl® C2101 is in particular suitable for (multi-layer) flexible products. Solanyl® C2191 can be mixed with most biopolyesters or starch based plastics to reduce costs. Solanyl® C2101 has a natural feel and look. Solanyl® C2101 is biodegradable with a biobased or plant based content of >40%. Applications are: Consumer goods & Packaging &Agriculture products Thermoform applications: Cups, boxes & trays Plates and sheets (outer-layers) Inner layer of groundwork applications like pipes Extruded flexible profiles |
技术参数 Technical Data | |||
---|---|---|---|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
200 到 1000 | µm | |
拉伸模量 Tensile modulus |
|||
MD MD |
350 到 450 | MPa | |
TD TD |
100 到 290 | MPa | |
拉伸强度 tensile strength |
|||
注塑成型 injection molding |
13.0 到 15.0 | MPa | ISO 527-2 |
MD,屈服 MD, yield |
13.0 到 17.0 | MPa | |
TD,屈服 TD, yield |
MPa | ||
MD MD |
MPa | ||
TD TD |
MPa | ||
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
MD MD |
N | ||
TD TD |
N | ||
水气透过率 Water vapor transmittance 3 |
|||
23℃,75% RH 23℃,75% RH |
g/m²/24 hr | ||
23℃,85% RH 23℃,85% RH |
g/m²/24 hr | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
注塑成型 injection molding |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
注塑成型 injection molding |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
注塑 Injection molding |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
注塑 Injection molding |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Water Activity Water Activity |
内部方法 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,注塑成型 Shaw's D, injection molding |
ISO 868 | ||
拉伸应变 Tensile strain |
|||
屈服,注塑成型 Yield, injection molding |
% | ||
断裂,注塑成型 Fracture, injection molding |
% | ||
弯曲模量 Bending modulus |
|||
注塑成型 injection molding |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
注塑成型 injection molding |
MPa | ISO 178 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
表观密度 Apparent density |
g/cm³ | ISO 60 | |
熔体质量流动速率 Melt Flow Rate |
|||
170℃,5.0kg 170℃,5.0kg |
g/10min | ISO 1133 | |
熔体体积流动速率 Melt Volume Rate |
|||
190℃,2.16 kg 190℃,2.16 kg |
cm³/10min | ISO 1133 | |
螺旋流动长度 Spiral flow length 2 |
cm | ||
收缩率 Shrinkage rate |
% | ISO 294-4 | |
含水量 water content |
内部方法 | ||
灰份含量 Ash Content |
% | 内部方法 | |
熔体表观粘度 Apparent viscosity of melt |
|||
140℃,10.0 sec^-1 140℃,10.0 sec^-1 |
Pa·s | ||
140℃,100 sec^-1 140℃,100 sec^-1 |
Pa·s | ||
140℃,1000 sec^-1 140℃,1000 sec^-1 |
Pa·s | ||
170℃,10.0 sec^-1 170℃,10.0 sec^-1 |
Pa·s | ||
170℃,100 sec^-1 170℃,100 sec^-1 |
Pa·s | ||
170℃,1000 sec^-1 170℃,1000 sec^-1 |
Pa·s | ||
特殊值 |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
MD,屈服 MD, yield |
% | ||
TD,屈服 TD, yield |
% | ||
MD,断裂 MD, fracture |
% | ||
TD,断裂 TD, fracture |
% | ||
注塑成型 injection molding |
MPa | ||
正割,注塑成型 Cutting, injection molding |
MPa |
备注 |
---|
2、模具温度: 25°C |
3、40-55 µm |
【新闻资讯】查看全部
云南:重点管控区域内化工企业全部达到最严格安全环保标准
2022-05-19 5月13日,云南省发展和改革委员会就《云南省十四五长江经济带化工污染治理工作方案(征求意见稿)》向社会公开征求意见。 《方案》明确,到 2025年,长江经济带化工污染治理深入 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |