牌号简介 About |
---|
10熔融聚碳酸酯,无氯无溴,用紫外线照射并释放。应用/用途:消费品、电器、工业产品、手工工具关键词:聚合物;热塑性塑料;聚碳酸酯(PC);聚碳酸酯,未增强,UL认可,UL 746H 10 Melt Polycarbonate, Non-Chlorine Non-Bromine, with UV and release. Application/Use: Consumer products, Appliances, Industrial products, Hand Tools Key Words: Polymer; Thermoplastic; Polycarbonate (PC); Polycarbonate, Unreinforced, UL Recognized, UL 746H |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
10 | g/10min | ASTM D1238 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.15 | % | ASTM D570 |
室外适用性 Outdoor applicability |
f1 | UL 746C | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
640 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~95℃ MD:-40~95℃ |
1/℃ | ||
TD:-40~95℃ TD:-40~95℃ |
1/℃ | ||
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 Electrical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
耐电弧性 Arc resistance |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
|||
1.5 mm 1.5 mm |
|||
3.0 mm 3.0 mm |
|||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
|||
1.5 mm 1.5 mm |
|||
3.0 mm 3.0 mm |
|||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
UL Rating UL Rating |
|||
Non-bromine,Non-chlorine Non-bromine,Non-chlorine |
UL 746H | ||
RoHS Compliance RoHS Compliance |
UL 746R | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength |
|||
屈服,3.17 mm Yield, 3.17 mm |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,3.17 mm Fracture, 3.17 mm |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
3.17 mm 3.17 mm |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服,3.17 mm Yield, 3.17 mm |
MPa | ASTM D790 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
科研人员仿生创造水用强力胶黏剂
2015-12-03 贻贝等贝类能够分泌出粘性很高的蛋白,借助这种物质它们能够牢牢地附着在岩石或船体上,任凭风吹浪打都不会脱落。日前美国加州大学圣芭芭拉分校(UC Santa Barbara)的研究人员受贻贝的启发,利用强大的合成材料开发出了一种粘性很强的水下粘合剂。这种超薄材料制成的水下粘合剂据说比此前的同类产品粘性至少高出10倍,其低分子量和功能特性意味着能大大提高现有粘合剂的性能,同时有望被用于牙医业、纳米技术、水下维修等领域。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |