| 牌号简介 About |
|---|
| 鲁米新MPE4040是以己烯为共聚单体的第二代茂金属基聚乙烯。与传统的LLDPE和第一代茂金属基聚乙烯相比，鲁米新MPE M 4040的挤出压力低、缩颈低、拉伸性能好、表观控制能力强。高刚度结合良好的光学性能带来了显著的测量潜力。Lumicene MPE M 4040是一种多用途树脂，可用于纯树脂或混合树脂，用于生产单层和多层膜。主要用途有：特种薄膜、卫生薄膜、压花薄膜、复合材料及消费品和自动包装，如生产袋、邮寄和卫生包装薄膜等。 Lumicene® mPE M 4040 is a second generation metallocene based Polyethylene with hexene as comonomer. Lumicene® mPE M 4040 can be processed at high output rates with low extrusion pressure, low neck-in, excellent drawability and gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The high stiffness combined with excellent optical properties brings a significant down-gauging potential. Lumicene® mPE M 4040 is a versatile resin that can be used in pure or in blend for the production of both monolayer and multilayer film. Main applications are: specialty film, hygiene film, embossed film, compounds and consumer and automatic packaging, such as produce bags, mailing and hygiene overwrap film. |
产品描述 Product Description
用途：薄膜;多层薄膜;包装;袋子;流延薄膜;混合;
加工条件：流延薄膜
性能特点： 机械强度好; 抗氧化; 内缩量低; 己烯共聚单体; 易剥离; 良好的测量控制; 光学性能; Good Rigidity,Good dissection,Good Gauge Control,Low shrinkage,Inoxidizability,Hexene copolymers
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
0.940 | g/cm³ | ISO 1183 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
190℃，2.16kg 190℃，2.16kg |
4.0 | g/10min | ISO 1133 |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
20 | µm | |
|
拉伸强度 tensile strength |
|||
|
MD，屈服，20 µm，吹塑薄膜 MD, yield, 20 µ m, blow molded film |
14.5 | MPa | |
|
TD，屈服，20 µm，吹塑薄膜 TD, yield, 20 µ m, blow molded film |
14.7 | MPa | |
|
MD，断裂，20 µm，吹塑薄膜 MD, fracture, 20 µ m, blow molded film |
MPa | ||
|
TD，断裂，20 µm，吹塑薄膜 TD, fracture, 20 µ m, blow molded film |
MPa | ||
|
拉伸应变 Tensile strain |
|||
|
MD，断裂，20 µm，铸造薄膜 MD, fracture, 20 µ m, cast thin film |
% | ||
|
TD，断裂，20 µm，铸造薄膜 TD, fracture, 20 µ m, cast thin film |
% | ||
|
落锤冲击 Drop hammer impact |
|||
|
20 µm，铸造薄膜 20 µ m, cast thin film |
g | ISO 7765-1 | |
|
埃尔曼多夫抗撕强度 Elmandorf tear strength |
|||
|
MD：20 µm，铸造薄膜 MD: 20 µ m, cast thin film |
N | ||
|
TD：20 µm，铸造薄膜 TD: 20 µ m, cast thin film |
N | ||
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
|
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
|
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
光泽度 gloss |
|||
|
45°，20 µm，铸造薄膜 45 °, 20 µ m, cast thin film |
ASTM D2457 | ||
|
雾度 Haze |
|||
|
20.0 µm，铸造薄膜 20.0 µ m, cast thin film |
% | ISO 14782 | |
| 备注 | |||
|---|---|---|---|
| 暂无数据 | |||
|
【新闻资讯】查看全部 
HP-RTM在意大利的最新进展
2018-01-17 RIBA复合材料公司是意大利一家领先的结构件与零部件制造商，主要为汽车和航空工业提供先进的复合材料零部件，最近购买了一套康隆(Cannon)新的HP-RTM和模压成型技术的生产线。 位于意大利法恩扎的RIBA复合材料公司原来一直采用热压罐和真空袋或真空炉小批量地生产复合材料零部件，现在，这家公司要扩大其汽车和航空领域的复合材料零部件产量。该公司原有的生产设备和工艺已无法满足汽车工业的系列化和规模化的生产需要，所以决定马上探索高产量的生产工艺，如HP-RTM和模压成型工艺。< |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
电邮一份说明书
PDF文档名：搜料网-TOTAL Polyethylene Lumicene® M 4040 (Cast Film)证书
发送至：（多个地址，中间以逗号隔开）
发送一份副本给我：您还没有填写邮箱!(点击完善资料)
当前牌号已加入对比
支付宝
微信支付