| 牌号简介 About |
|---|
| BX-31是一个由两部分组成的聚氨酯成型系统。BX-31混合100 ISO:97重量治愈（或1 pt-a ISO到1 pt-b体积治愈）并在室温下治愈。BX-31固化至低硬度，肖氏A 31±2，浅黄色橡胶。在室温固化3-4天后，获得最终性能。可通过加热（130-150°F，12-16小时）加速固化，但可获得稍硬的聚合物（34+/-2邵尔A），并可获得轻微收缩。应用程序BX-31用于制造包含中等咬边的母版模具。BX-31的物理性能使其非常适合制作详细的混凝土模具、模型和模板内衬。 BX-31 is a two-part polyurethane molding system. BX-31 is mixed 100 iso:97 curative by weight (or 1 Pt-A Iso to 1 Pt-B Curative by volume) and cures at room temperature. BX-31 cures to a low hardness, Shore A 31±2, light yellow rubber. Ultimate properties are obtained after 3-4 days of room temperature cure. Cure can be accelerated with heat (130-150°F for 12-16 hours) but a slightly harder polymer (34 +/- 2 Shore A) and slight shrinkage will be obtained. Applications BX-31 is used to make molds of masters that contain moderate undercuts. BX-31's physical properties make it ideal for making detailed concrete molds, patterns and formliners. |
产品描述 Product Description
用途：模具制造;模板;
性能特点： 室温固化; 低硬度; Low Hardness,Room Temperature Cure
| 技术参数 Technical Data | |||
|---|---|---|---|
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
脱模时间 stripping time |
|||
|
24℃ 24℃ |
1400 | min | |
|
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
颜色 colour |
|||
|
-- -- 2 |
Colorless Clear, Light Yellow | ||
|
-- -- 3 |
Yellow, Light | ||
|
重量混合比（PBW） Weight Mix Ratio (PBW) |
|||
|
Part A Part A |
100 | ||
|
Part B Part B |
97 | ||
|
体积混合比（PBV） Volume Mixing Ratio (PBV) |
|||
|
Part A Part A |
|||
|
Part B Part B |
|||
|
密度 Density |
|||
|
24℃ 24℃ 3 |
g/cm³ | ||
|
24℃ 24℃ 2 |
g/cm³ | ||
|
粘度 viscosity |
|||
|
24℃ 24℃ 3 |
Pa·s | ||
|
24℃ 24℃ 2 |
Pa·s | ||
|
固化时间 Curing time |
|||
|
24℃ 24℃ |
hr | ||
|
胶凝时间 Gelation time |
|||
|
24℃ 24℃ |
min | ||
|
储存稳定性 storage stability |
|||
|
24 ℃ 24 ℃ |
min | ||
|
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
邵氏硬度 Shore hardness |
|||
|
邵氏 A Shaw's A |
|||
|
拉伸强度 tensile strength |
MPa | ASTM D412 | |
|
拉伸应变 Tensile strain |
|||
|
断裂 fracture |
% | ASTM D412 | |
|
撕裂强度 tear strength |
|||
|
-- -- 4 |
kN/m | ASTM D470 | |
|
Die C Die C |
kN/m | ASTM D624 | |
| 备注 |
|---|
| 2、Part A |
| 3、Part B |
| 4、Split |
|
【新闻资讯】查看全部 
LG研发出新型可折叠显示屏材料，表面坚硬如玻璃 折叠部分柔韧像塑料
2021-09-09 搜料网资讯： 9月8日消息，据媒体报道，LG化学宣布成功研发出了一种可用于折叠屏的新材料，LG将其命名为Real Folding Window。 这款产品采用最新的涂层材料， 表面坚硬如玻璃，折叠部分 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付