| 牌号简介 About |
|---|
| Solanyl® C2003是一种适合挤压的端部化合物。Solanyl® C2003可以在传统的挤压生产线上加工。Solanyl® C2003是目前使用的可生物降解塑料的竞争替代品，如广泛应用的PP&PS。Solanyl® C2003可与大多数生物聚酯或淀粉基塑料混合，以降低成本。Solanyl® C2003拥有自然的感觉和外观。Solanyl® C2003是可生物降解的，生物基或植物基含量大于60%（也可提供少量溢价约70%）。可使用Solanyl C2003的应用包括：消费品和包装农产品热成型应用、杯、盒和托盘、板材和片材基础应用，如管道挤压型材。 Solanyl® C2003 is an end compound suitable for extrusion. Solanyl® C2003 can be processed on conventional extrusion lines. Solanyl® C2003 is a competitive alternative for currently used biodegradable plastics, like PP & PS for a wide range of applications. Solanyl® C2003 can be mixed with most biopolyesters or starch based plastics to reduce costs. Solanyl® C2003 has a natural feel and look. Solanyl® C2003 is biodegradable and has a biobased or plant based content of >60% (at a small premium ~70% can be delivered as well). Applications in which Solanyl ® C2003 can be used are: Consumer goods & Packaging Agriculture products Thermoform applications Cups, boxes & trays Plates and sheets Groundwork applications like pipes Extruded profiles |
产品描述 Product Description
用途：杯子;片材;包装;型材;托盘;热成型应用;农业应用;管道系统;
加工条件：挤出 Extrusion
性能特点： 可回收; 可堆肥; 食品接触; 生物可降解; Renewable resources,Biodegradable,Food contact compliance,Compostable
| 技术参数 Technical Data | |||
|---|---|---|---|
|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
密度 Density |
1.25 到 1.30 | g/cm³ | ISO 1183 |
|
表观密度 Apparent density |
0.70 到 0.80 | g/cm³ | ISO 60 |
|
熔体质量流动速率 Melt Flow Rate |
|||
|
170℃，2.16kg 170℃，2.16kg |
2.0 到 4.0 | g/10min | |
|
螺旋流动长度 Spiral flow length 2 |
22.0 到 40.0 | cm | |
|
收缩率 Shrinkage rate |
< 2.0 | % | ISO 294-4 |
|
含水量 water content |
内部方法 | ||
|
灰份含量 Ash Content |
% | 内部方法 | |
|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
拉伸模量 Tensile modulus |
|||
|
注塑成型 injection molding |
MPa | ||
|
正割，注塑成型 Cutting, injection molding |
MPa | ||
|
拉伸应变 Tensile strain |
|||
|
屈服，注塑成型 Yield, injection molding |
% | ||
|
断裂，注塑成型 Fracture, injection molding |
% | ||
|
弯曲模量 Bending modulus |
|||
|
注塑成型 injection molding |
MPa | ISO 178 | |
|
弯曲强度 bending strength |
|||
|
注塑成型 injection molding |
MPa | ISO 178 | |
|
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
薄膜厚度 film thickness |
|||
|
测试 test |
µm | ||
|
拉伸模量 Tensile modulus |
|||
|
MD MD |
MPa | ||
|
TD TD |
MPa | ||
|
拉伸强度 tensile strength |
|||
|
注塑成型 injection molding |
MPa | ISO 527-2 | |
|
MD，屈服 MD, yield |
MPa | ||
|
TD，屈服 TD, yield |
MPa | ||
|
MD MD |
MPa | ||
|
TD TD |
MPa | ||
|
拉伸应变 Tensile strain |
|||
|
MD，屈服 MD, yield |
% | ||
|
TD，屈服 TD, yield |
% | ||
|
MD，断裂 MD, fracture |
% | ||
|
TD，断裂 TD, fracture |
% | ||
|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
|
注塑成型 injection molding |
kJ/m² | ISO 179/1eA | |
|
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
|
注塑成型 injection molding |
kJ/m² | ISO 179/1eU | |
|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
热变形温度 Hot deformation temperature |
|||
|
1.8 MPa，未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
|
玻璃化转变温度 Glass transition temperature |
℃ | DSC | |
|
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
|
熔融温度 Melting temperature |
|||
|
DSC DSC |
℃ | 内部方法 | |
|
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
|
Water Activity Water Activity |
内部方法 | ||
| 备注 |
|---|
| 2、模具温度: 25°C, 熔体温度: 170 到 190°C |
|
【新闻资讯】查看全部 
高迸发期！河南辉县一化工厂发作燃爆 致1人死亡
2019-10-28 从河南辉县市政府网获悉，2019年10月25日7时50分左右，辉县市胡桥办事处永大化工厂一混合溶剂贮罐发生燃爆，事故造成一人死亡。 事故发生后，辉县市委、市政府主要领导，以及胡桥 |
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。 |
当前牌号已加入对比
支付宝
微信支付