Epsilon Pro是一种触变环氧涂层,可自增厚,用于刷涂各种表面。与原有的Epsilon相比,Epsilon Pro具有更长的工作时间,固化的环氧树脂是半刚性的,具有更好的抗冲击性。Epsilon Pro的混合比为体积比2a:1b(重量比100a:44b)。使用本产品不需要克标度。在薄层中,混合材料保持一个垂直的表面,没有下垂或坍塌。材料在不同表面上均匀浸湿。适用期为22分钟,再涂时间为3小时。应允许所有层在73°F/23°C下固化16小时,并且可以用温和的热加速。Epsilon Pro是透明的,可以很容易地使用如此强烈的着色剂、着色剂或uvo着色剂着色。固化后的涂层有光泽,可以用砂纸打磨、涂底漆和油漆。用途:εPro适用于EPS或聚氨酯泡沫的保护、耐冲击涂层。它也可以应用于灰泥、混凝土、木材和织物。本产品对湿度不敏感,不含挥发性有机化合物。 Epsilon® PRO is a thixotropic epoxy coating that self-thickens for brushing onto a variety of surfaces. Compared to original Epsilon®, Epsilon® PRO offers a longer working time and cured epoxy is semi-rigid, offering better impact resistance. Mix ratio for Epsilon® PRO is 2A:1B by volume (100A:44B by weight). A gram scale is not needed to use this product. Applied in thin layers, mixed material holds a vertical surface without sagging or slumping. Material wets out uniformly over different surfaces. Pot life is 22 minutes, with a re-coat time of 3 hours. All layers should be allowed to cure for 16 hours at 73° F / 23° C and can be accelerated with mild heat. Epsilon® PRO is clear and can be easily colored using SO-Strong®, Ignite® or UVO® colorants. Cured coating has a gloss finish and can be sanded, primed and painted. Applications: Epsilon® PRO is suitable for use as a protective, impact resistant coating for EPS or polyurethane foam. It can also be applied to plaster, concrete, wood and fabrics. This product is not sensitive to moisture / humidity and contains no VOC's. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
1.11 | g/cm³ | ASTM D1475 |
特定体积 Specific volume 2 |
0.903 | cm³/g | ASTM D792 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
65 | ASTM D2240 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
储存稳定性 storage stability |
22 | min | ASTM D2471 |
热固性混合粘度 Thermosetting mixed viscosity |
4000 | cP | ASTM D2393 |
脱模时间 stripping time 3 |
min | ||
Tack Free Time(Thin Film) Tack Free Time(Thin Film) |
hr | ||
工作时间 working hours |
|||
Thin Film Thin Film |
min | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
混合比 Mixing ratio |
|||
Tack-up Time - Thin Film - Recoat Tack-up Time - Thin Film - Recoat |
hr |
备注 |
---|
2、Mixed |
3、Cure Time |
【新闻资讯】查看全部
盒马创新优化效劳鼓舞消费者环保消费
2019-02-19 据2月14日消息,盒马宣布将启动绿色盒区计划,通过优化流程和供应链环节,减少从源头到餐桌塑料制品的使用。这个计划包含了绿色消费、绿色供应链、绿色回收三个部分,预计目标全年减少使用塑料380万公斤。 据易佰店淘宝店铺出售了解,盒马致力于探索用模式创新优化服务。为了鼓励消费者在门店环保消费,盒马还联合蚂蚁森林,消费者只要用盒马APP结账并且没有购买塑料袋,每天可获得21g蚂蚁森林绿色能量。预计2019年全年,可减少超过1277万只塑料袋的使用。 此外,盒马将继续 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |