GI-1120是一种高撕裂强度、锡催化的RTV-2硅橡胶,设计用于铸造聚酯零件。GI-1120特别适用于深底切的模具和需要弯曲以拆卸零件的模具。GI-1120对抑制不敏感,这意味着它几乎可以在任何表面上在室温下固化。它很容易混合和脱气,并将固化只有轻微的收缩。橡胶硬化的速度可以用特殊的活化剂来加速。冷凝固化双组分硅橡胶非常适合大多数一般的模具制造和原型应用。它们非常适合铸造蜡、石膏、环氧树脂和其他塑料。GI-1120非常适用于需要高延伸率和中等硬度的应用。 GI-1120 is a high tear strength, tin-catalyzed RTV-2 silicone rubber, which was designed for casting polyester parts. GI-1120 is especially good for molds with deep undercuts and for molds that require flexing for part removal. GI-1120 is not sensitive to inhibition, meaning it will cure at room temperature over virtually any surface. It is easy to mix and de-air, and will cure with only a slight degree of shrinkage. The speed at which the rubber hardens can beaccelerated with special activators. Condensation cure two-component silicone rubbers are excellent for most general mold making and prototype applications. They are excellent for casting waxes, gypsum, epoxies and other plastics. GI-1120 is extremely useful for those applications where superior elongation and medium durometer are required. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.08 | g/cm³ | |
收缩率 Shrinkage rate |
|||
Cured Cured |
0.10 | % | |
热固性混合粘度 Thermosetting mixed viscosity |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
颜色 colour |
|||
-- -- 2 |
Blue | ||
-- -- 3 |
Off White | ||
粘度 viscosity |
|||
-- -- 2 |
0.30 到 0.40 | Pa·s | |
-- -- 3 |
Pa·s | ||
固化时间 Curing time |
hr | ||
储存稳定性 storage stability |
min | ||
Cured Properties Cured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A 4 |
|||
邵氏 A Shaw's A 5 |
|||
拉伸强度 tensile strength |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength |
kN/m | ASTM D624 | |
Coverage(Cured) Coverage(Cured) |
cm³/g | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
使用温度 Operating temperature |
|||
Cured Cured |
℃ | ||
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
|||
贮藏期限 Storage period |
wk |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Activator |
3 Base |
4 1 Day |
5 7 Days |
【新闻资讯】查看全部
英国脱欧打击大宗商品市场 PVC等种类跌幅或超3%
2016-06-30 受脱欧事件影响,国际原油、铝等大宗商品出现暴跌――WTI一度跌破47美元/桶,下跌幅度超过6%,伦铜、伦铝跌幅均超过2%。国内期货市场相对“冷静”,截至记者发稿时铜、铝主力合约跌幅均未超过1%,塑料、煤焦等板块不跌反涨,棉花主力合约甚至盘中创出18个月来新高。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |