牌号简介 About |
---|
EVA共聚物Alcudia PA-538适用于挤出和注塑应用。这种材料兼具柔韧性和韧性。它含有抗氧化添加剂。典型应用挤出吹塑注射成型微孔泡沫建议熔融温度低于200°C,以避免聚合物分解。各生产线的加工条件应得到优化。 EVA copolymer ALCUDIA® PA-538 is suitable for extrusion and injection moulding applications. This material combines flexibility and toughness. It contains antioxidant additives. TYPICAL APPLICATIONS Extrusion Blow moulding Injection moulding Microcellular foams Recommended melt temperature below 200°C to avoid the decomposition of the polymer. Processing conditions should be optimised for each production line. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.937 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.0 | g/10min | ISO 1133 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
F50 F50 |
> 300 | hr | ASTM D1693 |
醋酸乙烯含量 Vinyl acetate content |
18.0 | wt% | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
64.0 | ℃ | ISO 306/A |
熔融温度 Melting temperature |
℃ | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A Shaw's A |
|||
邵氏 D Shaw's D |
|||
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
我国首个自营深水大气田“深海一号”建成投产
2021-06-27 搜料网资讯: 25日自中国海油获悉,由中国自营勘探开发的首个1500米超深水大气田深海一号在海南岛东南陵水海域正式投产,标志着中国海洋石油勘探开发能力全面进入超深水时代。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |