牌号简介 About |
---|
壁厚0.250"时20%减重。7.5% 玻纤增强。韧性好,耐化学性,低翘曲 |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,6.35 mm Yield, 6.35 mm |
46 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂,6.35 mm Fracture, 6.35 mm |
5.4 | % | ASTM D638 |
拉伸模量 Tensile modulus |
|||
6.40 mm 6.40 mm |
2990 | MPa | ASTM D638 |
弯曲强度 bending strength |
|||
屈服,6.40 mm Yield, 6.40 mm |
80 | MPa | ASTM D790 |
弯曲模量 Bending modulus |
|||
6.40 mm 6.40 mm |
3200 | MPa | ASTM D790 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
泡沫 Foam |
|||
阻燃6.4mm Wt 还原 Flame retardant 6.4mm Wt reduction |
g/cm³ | - | |
电气6.4mm Wt 还原 Electrical 6.4mm Wt reduction |
% | - | |
物理6.4mm Wt 还原 Physical 6.4mm Wt reduction |
% | - | |
热6.4mm Wt 还原 Hot 6.4mm Wt reduction |
% | - | |
机械6.4mm Wt 还原 Mechanical 6.4mm Wt reduction |
% | - | |
冲击6.4mm Wt 还原 Impact 6.4mm Wt reduction |
% | - | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
J/m | ASTM D 4812 | |
落锤冲击 Drop hammer impact |
|||
23℃ 23℃ |
J | 内部方法 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
未退火,6.4 mm Unannealed, 6.4 mm |
|||
0.45 MPa 0.45 MPa |
℃ | ASTM D 648 | |
1.8MPa 1.8MPa |
℃ | ASTM D 648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~95℃ MD:-40~95℃ |
1/℃ | ASTM E831 | |
比热 specific heat |
J/g-℃ | ASTM C 351 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746B | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746B | |
非机械冲击性能 Non mechanical impact performance |
℃ | UL 746B | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
- | ASTM D 792 | |
泡沫成型 Foam molding |
ASTM D792 | ||
吸水率 Water absorption rate |
|||
平衡,23℃ Equilibrium, 23 ℃ |
% | ASTM D570 | |
24hr 24hr |
% | ASTM D570 | |
收缩率 Shrinkage rate |
|||
MD:6.4 mm MD:6.4 mm |
% | 内部方法 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
表面电阻率 Surface resistivity |
ohms/sq | ASTM D257 | |
相对电容率 Relative permittivity |
|||
100 Hz 100 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D50 | ||
耗散因数 Dissipation factor |
|||
100 Hz 100 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耐电弧性 Arc resistance |
|||
钨丝 Tungsten wire |
PLC Code | ASTM D495 | |
高电压弧起痕速率{PLC} High voltage arc marking rate {PLC} |
PLC Code | UL 746A | |
相比漏电起痕指数 Compared to the leakage tracing index |
PLC Code | UL 746A | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级94HB Flame retardant grade 94HB |
mm | UL 94 | |
紫外线 ultraviolet radiation |
|||
水暴露/浸没 Water exposure/immersion |
- | UL 746C |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部 ![]()
2022年1月份ABS/PS装置检修情况简析
2022-02-11 从最新跟踪的情况来看,2022年首月,ABS/PS停车检修的企业仅4家,涉及产能76万吨。临近春节假期,贸易商开始准备放假,在下游需求没有明显好转,减弱预期的情况下,多按需采购为主 |
|||||||||||||||||||||||||||||||||
2022年1月份ABS/PS装置检修情况简析 从最新跟踪的情况来看,2022年首月,ABS/PS停车检修的企业仅4家,涉及产能76万吨。临近春节假期,贸易商开始准备放假,在下游需求没有明显好转,减弱预期的情况下,多按需采购为主。因此在市场报价货源有限的情况下,装置停车检修对行情走势的影响并不明显。
表1:1月国内ABS生产企业装置变动表 1月,国内ABS装置开工率较高,除漳州奇美维持五线生产,开工八成左右;广西长科低负荷生产;其余ABS厂家维持正常生产。从表1我们看到,春节期间整体检修厂家并不多,部分厂家检修主要受冬奥会的不可抗力影响。其中,天津大沽预计会降负荷生产,减产3-4成;山东海江2月份存减产计划,整月产量预计减少30%左右,3月份ABS装置计划内检修,预计全部停车;LG惠州厂家计划于2022年2月份对二期装置检修18天,3月份对一期装置检修11天,主要为装置管道检修。其15万吨/年扩能计划推至3-4月份。
表2:1月国内PS生产企业装置变动表 受淡季影响,加之春节期间物流运输受限,本月国内个别装置或长或短停车放假。如表2所示,中信国安1月7日七透一改生产,1月21日六透两改生产;星辉环材12月29日透苯线停车检修,1月8日重启;惠州仁信1月13日晚间对两条透苯线停车检修,1月17日两透一改生产,1月27日一透一改生产,春节期间两线生产;山东玉皇开工七成左右;其他石化企业装置正常生产。春节期间,绿安擎峰1月30日停车,2月20日重启;昌亚石化1月30日左右停车检修,时长1个月左右;天津仁泰听闻2月份装置减产两成左右。山东玉皇、山东道尔、山东岚化PS装置暂无明确春节假期检修计划。 在成本支撑和需求压制下,1月ABS/PS行情总体偏弱。节假日、疫情、低温、冬奥会等影响下,春节期间行情变动有限。节后下游整体复工速度尚未可知,行业新投产释放是否存预期,多种不确定因素仍需我们关注,建议商家谨慎操盘。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。