牌号简介 About |
---|
Durethan® BC 550 Z DUSXBL 900116 是非增强的PA 6材料,用吹塑成型加工的方式进行加工,具有优良的抗冲击性能和热老化稳定性。在用于储罐系统和压力容器时注意安全。 Durethan® BC550Z 900116 DUSXBL (Dry) PA 6, non-reinforced, blow molding, improved impact strength, heat-aging stabilized. For the use in tank systems and pressure vessels please notice safety-related technical information within the High Performance Materials TechCenter under www.durethan-tank-systems.lanxess.com . Durethan® BC550Z 900116 DUSXBL PA 6, non-reinforced, blow molding, improved impact strength, heat-aging stabilized. For the use in tank systems and pressure vessels please notice safety-related technical information within the High Performance Materials TechCenter under www.durethan-tank-systems.lanxess.com . Durethan® BC550Z 900116 DUSXBL PA 6, non-reinforced, blow molding, improved impact strength, heat-aging stabilized. For the use in tank systems and pressure vessels please notice safety-related technical information within the High Performance Materials TechCenter under www.us.durethan-tank-systems.lanxess.com . |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.07 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD:260℃,2.0 mm TD:260℃,2.0 mm 2 |
1.5 | % | ISO 294-4 |
TD:120℃,2.0 mm,2 hrs TD:120℃,2.0 mm,2 hrs 3 |
0.20 | % | ISO 294-4 |
MD:260℃,2.0 mm MD:260℃,2.0 mm 2 |
1.5 | % | ISO 294-4 |
MD:120℃,2.0 mm,2 hrs MD:120℃,2.0 mm,2 hrs 3 |
0.20 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/50 | |
标称拉伸断裂应变 Nominal tensile fracture strain |
|||
23℃ 23℃ |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 4 |
|||
23℃ 23℃ 4 |
MPa | ISO 178-A | |
弯曲强度 bending strength 4 |
|||
3.50% 应变 3.50% strain |
MPa | ISO 178-A | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲应变 Bending strain 5 |
% | ||
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
膜刺穿强度 Membrane puncture strength |
ISO 6603-2 | ||
-- -- 6 |
J | ISO 6603-2 | |
-- -- 7 |
J | ISO 6603-2 | |
膜刺穿力 Membrane puncture force |
ISO 6603-2 | ||
-- -- 6 |
N | ISO 6603-2 | |
-- -- 7 |
N | ISO 6603-2 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
ISO 179/1eU | ||
23℃ 23℃ |
ISO 179/1eU | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ISO 180/1U | ||
-30℃ -30℃ |
ISO 180/1U | ||
23℃ 23℃ |
ISO 180/1U | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融温度 Melting temperature 5 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
ISO 1874 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 60x60x2; MT 80°C; 600 Bar |
3 60x60x2mm, 80°C MT, 600 bar |
4 60x60x2 |
5 60x60x2mm |
6 0.079 in/min |
7 2 mm/min |
8 Pull Rate: 2 mm/min; 50% RH |
9 -30°C |
10 23°C |
11 10°C/min |
【新闻资讯】查看全部
原油期权今日在上期能源挂牌交易
2021-06-21 搜料网资讯: 今日,上期所子公司上期能源将正式上市原油期权。 根据6月18日上期能源发布的《关于原油期权合约上市挂牌基准价的通知》,首批挂牌交易的原油期权合约的标的期货合 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |