牌号简介 About |
---|
甲烯烃甲氧基L7是一种高强度线性低密度己烯共聚物聚乙烯,采用气相法生产。与竞争性的超己烯LLDPE薄膜树脂相比,薄膜力学性能有显著提高。福尔马林福尔马克斯L7是一种具有防滑和防堵塞功能的配方,适用于高性能薄膜应用,具有优异的挤压加工性能、优异的冲击强度和抗撕裂性能。薄膜具有良好的光学性能。甲醛甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲氧基甲建议应用:工业包装工业衬垫共挤罐衬垫消费垃圾袋 Formolene FORMAX® L7 is a high strength linear low density polyethylene made using a gas-phase process. Film mechanical properties are significantly improved compared to competitive super hexene LLDPE film resins. Formolene FORMAX® L7 is formulated with slip and antiblock for use in high performance film applications offering excellent extrusion processing and outstanding impact strength and tear resistance. Films exhibit good optical properties. Formolene FORMAX® L7 meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact. Suggested Applications: Industrial Packaging Industrial Liners Coextrusion Can Liners Consumer Trash Bags |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.918 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.90 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
拉伸强度 tensile strength |
|||
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
29.6 | MPa | ASTM D882 |
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film |
11.2 | MPa | ASTM D882 |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ASTM D882 | |
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
|||
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709 | |
撕裂强度 tear strength |
|||
TD,25 µm,吹塑薄膜 TD, 25 µ m, blow molded film |
g | ASTM D1922 | |
MD,25 µm,吹塑薄膜 MD, 25 µ m, blow molded film |
g | ASTM D1922 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
丙烯市场多种生产工艺:甲醇制烯烃相对优势?
2015-11-27 随着全球经济的飞速发展,化工行业发展迅猛,世界各国对重要的石化原料丙烯的需求迅速增长。市场分析师表示,目前我国丙烯生产工艺三分天下,除了近几年迅速兴起的丙烷脱氢和煤制烯烃等新兴生产工艺之外,催化裂化和蒸汽裂解等传统工艺依然是目前我国丙烯最主要的来源,而丙烯作为重要的化工原料,其装置也是备受市场关注的。 油制丙烯:主要是副产品 油制丙烯属于老牌工艺,也是目前丙烯产能产量占比最多的,分为蒸汽热裂解和催化裂化两种,其中的相同点是丙 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |