牌号简介 About |
---|
热传导矿物和玻璃纤维填充PA6, FR,符合ECO协议,无溴,无氯 Thermally conductive mineral and glass fiber filled PA6, FR, compliant with ECO protocols, non-brominated, non-chlorinated |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.79 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
ASTM D955 | ||
MD:24 hrs MD:24 hrs |
0.42 | % | ASTM D955 |
TD:24 hrs TD:24 hrs |
0.58 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.23 | % | 内部方法 |
23℃,24hr 23℃,24hr |
0.040 | % | ISO 62 |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 3 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture 4 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 4 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 5 |
MPa | ASTM D790 | |
-- -- 6 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- 6 , 7 |
MPa | ISO 178 | |
屈服,50 mm跨度 Yield, 50 mm span 5 |
MPa | ASTM D790 | |
断裂,50 mm跨度 Fracture, 50 mm span 5 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
kJ/m² | ISO 179 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ 8 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
23℃ 23℃ 8 |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 9 |
℃ | ISO 75-2/Bf | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 9 |
℃ | ISO 75-2/Af | |
球压测试 Ball pressure test |
|||
125℃ 125℃ |
IEC 60695-10-2 | ||
线性热膨胀系数 Linear coefficient of thermal expansion |
ASTM E831 | ||
MD:40~120℃ MD:40~120℃ |
1/℃ | ASTM E831 | |
TD:40~120℃ TD:40~120℃ |
1/℃ | ASTM E831 | |
导热系数 Thermal conductivity coefficient |
|||
-- -- 10 |
W/m/K | ASTM E1461 | |
-- -- 11 |
W/m/K | ASTM E1461 | |
-- -- 12 |
W/m/K | ISO 22007-2 | |
-- -- 13 |
W/m/K | ISO 22007-2 | |
相对温度指数 Relative temperature index |
℃ | UL 746 | |
电气性能 Electrical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
介电强度 Dielectric strength |
|||
1 mm,在油中 1 mm in oil |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
|||
1.10 GHz 1.10 GHz |
ASTM ES7-83 | ||
耗散因数 Dissipation factor |
|||
1.1 GHz 1.1 GHz |
ASTM ES7-83 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.80 mm 0.80 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.0-3.0 mm 1.0-3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
1 mm 1 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.20 in/min |
3 类型 1, 0.20 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Break |
7 80*10*4 |
8 80*10*4 mm |
9 through-plane, 10*10*3mm sample |
10 in-plane, ø25*0.4mm disc |
11 through-plane, ø80*3mm discs |
12 in-plane, ø80*3mm discs |
【新闻资讯】查看全部
巴西石油出口同比下降
2021-11-29 搜料网资讯: 近日,巴西外贸统计系统Comex Stat发布最新数据显示,在连续7年创历史新高后,今年巴西石油出口开始下滑,前9个月同比下跌4.5%。 作为巴西主要石油生产商,巴国家石油 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |