牌号简介 About |
---|
Eraclene® BC 82是一种高密度聚乙烯树脂(HDPE),含抗氧化剂,适用于吹塑应用。特别推荐用于生产高达20升的容器。Eraclene® BC 82具有良好的抗应力开裂性能、良好的刚性和冲击强度。该树脂具有较高的熔融强度和适度的膨胀。Eraclene® BC 82的特点是中间分子量分布,平衡了整体性能和易于加工。主要用途Eraclene® BC 82用于生产高速机器、家用和工业化学品(洗涤剂、漂白剂等)、化妆品(洗发水、面霜、乳液等)、保健和医疗辅助设备的吹塑容器。Eraclene® BC 82适用于薄壁件,可以挤压成型材和薄板。 Eraclene BC 82 is a high density polyethylene resin (HDPE), with antioxidants, suitable for blow moulding application. It is especially recommended for the production of containers up to 20 liters. Eraclene BC 82 combines a good stress cracking resistance with a good rigidity and impact strength. This resin exhibits a high melt strength together with a moderate swelling. Eraclene BC 82 is characterized by an intermediate molecular weight distribution which balances overall performances with ease of processing. Main Application Eraclene BC 82 is used to produce, with high-speed machines, blow moulded containers for household and industrial chemicals (detergents, bleaches, etc), cosmetics (shampoos, creams, lotions, etc.), health and medical aids. Eraclene BC 82 is suitable for thin wall items and can be extruded into profiles and sheets. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.954 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
ISO 1133 | ||
190℃,2.16kg 190℃,2.16kg |
0.25 | g/10min | ISO 1133 |
190℃,21.6kg 190℃,21.6kg |
23 | g/10min | ISO 1133 |
190℃,5.0kg 190℃,5.0kg |
0.90 | g/10min | ISO 1133 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
模压成型 Compression Molding |
> 60.0 | hr | ASTM D1693B |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,模压成型 Shaw's D, molded |
ISO 868 | ||
拉伸强度 tensile strength |
|||
断裂,模压成型 Fracture, molded |
MPa | ISO 527-2 | |
屈服,模压成型 Yield, molding |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,模压成型 Fracture, molded |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
模压成型 Compression Molding |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 2 |
|||
模压成型 Compression Molding 2 |
J/m | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
℃ | 内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 方法 A |
【新闻资讯】查看全部
阻燃剂成高分子资料重要助剂 受全球性注重
2016-08-26 近年来,高分子材料的应用领域逐步得以拓展。基于高分子材料的易燃性,阻燃剂的应用与研究受到了全球性的重视。作为降低材料着火能力的材料助剂,阻燃剂目前已经成为高分子材料的重要的助剂。 当前,全球四大阻燃剂市场分别为:美国、欧洲、日本以及其他亚太地区。在四个市场中,用量增长最快的是亚洲其他国家地区。资料显示,2006~2010年,全球阻燃剂用量的年均增长率为4.1%,而亚洲其他国家和地区年均增长率为12.5%。据预测,2008~2014年,全球阻燃剂用量的年平均增长率可达4.9% |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |