产品描述:H 125是一种高熔体流动速率均聚物,专为纺粘法非织造布设计。该树脂具有良好的加工性能,除了提高机械性能外,还能提高生产线速度或气压。窄的分子量分布,特殊的稳定性和严格的凝胶外观控制,提供了其独特的性能。用途:卫生一次性用品和医院用品用高性能纺粘非织造布;家具和装饰用非织造布;低标题和/或高速纺复丝。 H 125 is a high melt flow rate homopolymer designed for spunbond nonwoven production. This resin features an excellent processability, allowing increased line speed or air pressure, as well as gains of mechanical properties. The narrow molecular weight distribution, special stability and tight gel control, provide its unique performance. Applications: High-performance spunbond nonwovens for hygiene disposables and hospital products; Nonwovens for furniture and decoration; Low-title and/or high-speed spinning multifilaments. Processing: Fiber Extrusion |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.905 | g/cm³ | ASTM D792, ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
38 | g/10min | ASTM D1238,ISO 1133 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,注塑成型 23 ℃, injection molding |
25 | J/m | ASTM D256 |
23℃,注塑成型 23 ℃, injection molding |
2.7 | kJ/m² | ISO 180 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,注塑成型 0.45 MPa, unannealed, injection molded |
95.0 | ℃ | ASTM D648 |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
1.8 MPa,未退火,注塑 1.8 MPa, unannealed, injection molded |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A, ASTM D1525 1 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
R 级 R-level |
ISO 2039-2 | ||
拉伸强度 tensile strength |
|||
屈服,注塑成型 Yield, injection molding |
MPa | ASTM D638, ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服,注塑成型 Yield, injection molding |
% | ASTM D638, ISO 527-2 | |
弯曲模量 Bending modulus |
|||
1% 正割,注塑成型 1% cut, injection molding |
MPa | ASTM D790 | |
1% 正割,注塑成型 1% cut, injection molding |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 压 力1 (10N) |
【新闻资讯】查看全部
2021年能源经济强势攀升后回稳
2022-01-15 搜料网资讯: 1月9日,北京理工大学能源与环境政策研究中心在北京举行2022年能源经济预测与展望研究系列报告发布会。与会专家学者认为,2021年能源经济强势攀升后回稳,新能源行业 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |